Pengaruh Elektroplating Krom Terhadap Laju Korosi Kawat Tembaga Sebagai Penghantar dalam Larutan NaCl

The Effect of Chrome Electroplating On Corrosion Rate Of Copper Wire as Conductor in NaCl Solution

Tugas Akhir, 025 / 2018 / TKI
Undergraduate Theses from JBPTPPOLBAN / 2019-02-08 13:43:53
Oleh : 151411043 - Hana Amatullah karimah - 151411047 - Lora Trimigo Pangesti (hana.amatullah.tkim15@polban.ac.id)
Dibuat : 2019-02-08, dengan 4 file

Keyword : Elektroplating Krom Keras, Anoda Korban, Laju Korosi, Kawat tembaga.
Subjek : Hardchrome Electroplating, Sacrificial Anode, Corrosion Rate, Copper Wires

Salah satu metode untuk mengendalikan korosi adalah dengan proteksi katodik anoda korban. Logam yang akan dilindungi dihubungkan dengan logam yang lebih reaktif. Salah satu permasalahan pada proteksi katodik anoda korban adalah terkorosinya sambungan kabel tembaga yang terhubung dengan struktur. Korosi pada sambungan tersebut dapat memutuskan aliran arus dari anoda dan terjadi kegagalan proteksi. Untuk menghindari terputusnya sambungan anoda dengan struktur maka dilakukan penanganan dengan melakukan electroplating hardchrome pada kawat tembaga. Penelitian ini dilakukan untuk menentukan karakteristik tembaga setelah melalui tahapan elektroplating krom dan mengetahui pengaruh jenis anoda korban magnesium dan alumunium pada kawat tembaga. Penelitian dilakukan pada kabel tembaga dengan jenis AWG 6 yang disambungkan pada anoda korban dalam lingkungan larutan NaCl 3,5% selama 600 jam. Variasi yang digunakan yaitu tembaga dilapisi oleh lapisan krom keras dan tembaga tidak diberikan lapisan krom. Pemasangan tembaga pada anoda korban diberi variasi berupa dikaitkan dan dilas. Metode uji yang dilakukan adalah metode kehilangan berat untuk mengetahui laju korosi dan metode Metalografi. Hasil dari laju korosi pada kawat tembaga yang diberi lapisan krom keras yang dikaitkan dengan anoda korban Mg mengalami penurunan sebesar 59% sedangkan kawat tembaga yang diberi lapisan krom yang dilas dengan anoda korban Mg mengalami penurunan sekitar 48%. Hasil dari laju korosi pada kawat tembaga yang diberi lapisan krom keras yang dikaitkan dengan anoda korban Al mengalami penurunan sebesar 10,4% sedangkan kawat tembaga yang diberi lapisan krom keras dan dilas dengan anoda korban Al mengalami penurunan sebesar 7,4%.

Deskripsi Alternatif :

One of method for controlling corrosion is the sacrificial anode cathodic protection. The metal to be protected is connected to a more reactive metal. One of the problems with cathodic protection of sacrificial anodes is the corroding of copper cable connections connected to the structure. Corrosion to the connection can break the current flow from the anode and a protection failure occurs. To avoid breaking the anode connection with the structure, handling is done by electroplating hardchrome on copper wire. This research was conducted to determine the characteristics of copper after going through the stages of chrome electroplating and knowing the effect of the magnesium and aluminum sacrificial anode types on copper wire. The study was carried out on copper cable with AWG 6 type which was connected to the sacrificial anode in a 3.5% NaCl solution for 600 hours. The variation used is that copper is coated with a hard chrome layer and copper is not given a chrome coating. The installation of copper on the sacrificial anode is given a variation in the form of being linked and welded. The test method used is the weight loss method to determine the corrosion rate and the metallographic method. The results of the corrosion rate on copper wires which were given a hard chrome coating associated with Mg sacrificial anodes decreased by 59% while copper wire which was given a chrome coating welded with Mg sacrificial anodes decreased by about 48%. The results of the corrosion rate on copper wire given a hard chrome coating associated with Al sacrificial anodes decreased by 10.4% while copper wire which was given a hard chrome coating and welded with Al sacrificial anodes decreased by 7.4%.

Beri Komentar ?#(0) | Bookmark

PropertiNilai Properti
ID PublisherJBPTPPOLBAN
Organisasi
Nama KontakHelmi Purwanti
AlamatJl. Trsn. Gegerkalong Hilir Ds. Ciwaruga
KotaBandung
DaerahJawa Barat
NegaraIndonesia
Telepon022 201 3789 ext. 168, 169, 239
Fax022 201 3889
E-mail Administratorhelmi.purwanti@polban.ac.id
E-mail CKOhelmi.purwanti@polban.ac.id

Print ...

Kontributor...

  • Pembimbing: Ir. Yunus Topana S., M.T. , Editor: Muhammad Abdillah Islamy, S.Pd

Download...