Pengaruh Proses Die Drawing Terhadap Keausan Material Ultra High Molecular Weight Polyethylene Pada Uji Keausan Pin-On-Plate Dengan Material Stainless Steel SUS-316L

The Effect of Die Drawing Process on the Wear of Ultra High Molecular Weight Polyethylene (UHMWPE) Material Trough Pin-On-Plate Wear Test Paired with Stainless Steel SUS-316L

Journal from JBPTPPOLBAN / 2012-02-23 15:11:19
Oleh : Achmad Hatta
Dibuat : 2012-02-23, dengan 1 file

Keyword : UHMWPE, PBS, die drawing

Total knee joint prosthesis adalah penggantian sendi lutut secara menyeluruh dengan sendi lutut tiruan yang menggunakan biomaterial. Biomaterial yang digunakan harus mempunyai kemampuan untuk berinteraksi dengan sel tubuh manusia tanpa menimbulkan efek samping yang membahayakan tubuh manusia. Bagian ujung femoral dan tibia dibuang lalu diganti dengan material stainless steel SUS-316L dan Ultra High Molecular Weight Poly-Ethylene (UHMWPE). Tujuan penelitian ini adalah untuk melihat pengaruh proses die drawing pada material UHMWPE terhadap keausan. Material yang digunakan adalah stainless steel SUS-316L berupa pelat berukuran 50x15x3mm dan pin UHMWPE berdiameter 8 mm. Pada beberapa benda uji, SUS-316L diberi perlakuan implantasi ion berbasis nitrogen dan proses draw drawing pada UHMWPE. Alat yang digunakan dalam penelitian ini adalah mesin uji keausan unidirectional reciprocating pin on plate. Uji keausan dilakukan dalam beberapa periode waktu dan parameter yang berbeda-beda, yaitu: beberapa variant pasangan SUS-316L dengan dan tanpa perlakuan ion implantation serta UHMWPE dengan dan tanpa perlakuan die drawing. Uji keausan dilakukan menggunakan pelumas PBS, dengan jarak lintasan 15 km, 30 km, dan 35 km. Gaya penekanan digunakan pada pin 180 N. Faktor keausan tertinggi yang dihasilkan adalah 5,57x10-5, 1,43x 10-5 dan 1,36x1.0-5 mm3/N berturut-turut untuk pasangan material SUS-316L ion implantation - UHMWPE die drawn, SUS-316L virgin - UHMWPE die drawn serta SUS-316L ion implantation - UHMWPR virgin. Untuk dua pasangan material pertama yaitu UHMWPE dengan proses die drawing mempunyai faktor keausan yang jauh lebih kecil. Dapat disimpulkan bahwa proses die drawing pada material UHMWPE dapat dipertimbangkan untuk diaplikasikan pada penggantian sendi lutut tiruan dengan menggunakan material tersebut.

Deskripsi Alternatif :

Total knee joint prosthesis is a damage knee joint replacement system using artificial materials called bio-materials. A bio-material must be able to interact within human body cell without any negative effects for human body. Each end part of femoral and tibia are removed, then replaced using stainless steel SUS-316L and Ultra High Molecular Weight Poly-Ethylene (UHMWPE). The aim of this research was to observe the effects of die drawing process on UHMWPE subjected to unidirectional reciprocating pin-on-plate wear test. The materials which were used in this research was 8 mm diameter UHMWPE pin with and without die drawing process, and polished 50x15x4mm stainless steel SUS-316L plates with and without ion implantation process. A unidirectional reciprocating pin-on-plate wear testing machine was used to test some pairs of UHMWPE pin and SUS-316L plate for some periodic time. The wear test was using Phospate Buffered Saline (PBS) as lubricant and some variation parameters such travel distance, speed and force during the test. The travel distance variation were 15km, 30km and 35km, while the force was 180N. The wear factors for this research are research are 5,57x10-5, 1,43x 10-5and 1,36x1.0-5 mm3/N respectively for UHMWPE virgin SUS-316L ion implantation. SUS-316L ion implantation - UHMWPE die drawn, and SUS-316L virgin - UHMWPE die drawn. The die drawn UHMWPE gives much lower wear factor than virgin UHMWPE, which is almost 1/3 times of virgin UHMWPE therefore it can be considered as an artificial material process for knee joint prosthesis replacement.

Beri Komentar ?#(0) | Bookmark

PropertiNilai Properti
ID PublisherJBPTPPOLBAN
Organisasi
Nama KontakHelmi Purwanti
AlamatJl. Trsn. Gegerkalong Hilir Ds. Ciwaruga
KotaBandung
DaerahJawa Barat
NegaraIndonesia
Telepon022 201 3789 ext. 168, 169, 239
Fax022 201 3889
E-mail Administratorhelmi.purwanti@polban.ac.id
E-mail CKOhelmi.purwanti@polban.ac.id

Print ...

Kontributor...

  • , Editor: Idayu Gemalia

Download...