Sintesis Nitrogen-Doped Carbon Nanodots Dari Molase Menggunakan Metode Microwave-Assisted Extraction Untuk Mendegradasi Metilen Biru Secara Fotokatalitik

Synthesis Nitrogen-Doped Carbon Nanodots From Molasses Using Microwave-Assisted Extraction Method For Photocatalytic Degradation Of Methylene Blue

Tugas Akhir, 001 / 2019 / ANK
Undergraduate Theses from JBPTPPOLBAN / 2020-03-13 10:00:26
Oleh : Ahya Sularasa - 161431001 & Muhamad Ariq Al Badar - 161431020 (ariqalbadar14@gmail.com)
Dibuat : 2020-03-13, dengan 4 file

Keyword : Metilen Biru, N-doped Carbon Nanodots, Molase, Fotokatalitik
Subjek : Methylene Blue, N-doped Carbon Nanodots, Molasses, Photocatalytic

Pertumbuhan industri tekstil di Indonesia membawa dampak negatif bagi lingkungan karena semakin banyaknya pembuangan limbah cair yang masih mengandung zat warna berbahaya ke badan sungai yang dapat mengakibatkan terganggunya kehidupan biota air dan kesehatan masyarakat sekitar yang memanfaatkan air sungai untuk kebutuhan domestik. Untuk mengatasi permasalahan tersebut N-doped Carbon Nanodots (N-doped CNDs) hadir sebagai fotokatalis yang dapat digunakan sebagai alternatif dalam mendegrdasi MB melalui reaksi fotokatalitik. N-doped CNDs berbahan dasar molase dengan ukuran partikel 1,5 nm yang memiliki fluoresensi berwarna biru dibawah sinar UV 365 nm, memiliki puncak spektrum di panjang gelombang 220 nm, dan memiliki gugus OH, C-H, C=O, N-H, serta C-N dengan bilangan gelombang 3246,94 cm-1, 2929,06 cm-1, 1656,08 cm-1, 1590,27 cm-1, dan 1036,98 cm-1 telah berhasil disintesis menggunakan H2O2 yang dilanjut dengan metode Microwave Assisted Extraction (MAE). Keberhasilan doping nitrogen dibuktikan dengan hasil analisis mengguanakan FTIR yang menunjukkan adanya peningkatan absorbansi dari gugus C-N dan N-H pada N-doped CNDs. Potensi N-doped CNDs sebagai fotokatalis yang dimodifikasi dengan penambahan dopant nitrogen untuk mendegradasi metilen biru (MB) menjadi objek dari penelitian ini. Hasil menunjukkan bahwa efisiensi degradasi metilen biru mengunakan 3 mL N-doped CNDs pada pH 10 menunjukkan efisiensi degradasi yang paling optimal. Pada kondisi tersebut efisiensi degradasi yang dihasilkan dari penggunaan lampu UV 254 nm 11 W dan lampu LED Philips 14,5 W dalam waktu 270 menit adalah sebesar 96,8% dan 97,2%. Kata kunci: Metilen Biru, N-doped Carbon Nanodots, Molase, Fotokatalitik.

Deskripsi Alternatif :

The growth of the textile industry in Indonesia harms the environment due to the disposal of liquid waste that still contain dangerous dyes to the river bodies which can disrupt the life of aquatic biota and the health of surrounding communities that use river water for domestic needs. To overcome this problem N-doped Carbon Nanodots (N-doped CNDs) are present as photocatalysts which can be used as an alternative in degrading MB through photocatalytic. N-doped CNDs from molasses have been successfully synthesized using H2O2 followed by the Microwave-Assisted Extraction (MAE) method. The synthesized N-doped CNDs have 1,5 nm particle size, the blue fluorescence under UV 365 nm, and a spectrum peak at 220 nm wavelength. The O-H, C-H, C=O, N-H, and C-N groups with wavenumbers 3246,94 cm-1, 2929,06 cm-1, 1656,08 cm-1, 1590,27 cm-1, and 1036,98 cm-1 have been observed by FTIR. The increase of absorbance of C-N and N-H groups of N-doped CNDs is showed by FTIR analysis that proved the success of nitrogen doping which. The potential of N-doped CNDs as photocatalysts for photocatalytic degradation of methylene blue (MB) became the object of this study. The results showed that the degradation efficiency of methylene blue using 3 mL N-doped CNDs at pH 10 showed the most optimal degradation efficiency. Under these conditions the degradation efficiency resulting from the use of 254 nm 11 W UV lamps and 14,5 W Philips LED lamps in 270 minutes is 96,8% and 97,2%. Keywords: Methylene Blue, N-doped Carbon Nanodots, Molasses, Photocatalytic Keywords: Methylene Blue, N-doped Carbon Nanodots, Molasses, Photocatalytic.

Beri Komentar ?#(0) | Bookmark

PropertiNilai Properti
ID PublisherJBPTPPOLBAN
Organisasi
Nama KontakHelmi Purwanti
AlamatJl. Trsn. Gegerkalong Hilir Ds. Ciwaruga
KotaBandung
DaerahJawa Barat
NegaraIndonesia
Telepon022 201 3789 ext. 168, 169, 239
Fax022 201 3889
E-mail Administratorhelmi.purwanti@polban.ac.id
E-mail CKOhelmi.purwanti@polban.ac.id

Print ...

Kontributor...

  • Pembimbing 1: Haryadi, M.Sc., Ph.D.

    Pembimbing 2: Dra. Mentik Hulupi, M.S., Editor: Erlin Arvelina

Download...