Pembuatan Komposit Poliester Dengan Filler Serat Eceng Gondok Terasetilasi Dan Karbon

Manufacture Of Polyester Composite With Acetylation Hyacinth Fiber And Carbon As Filler

Skripsi, 003 / 2018 / KPB
Undergraduate Theses from JBPTPPOLBAN / 2018-09-25 12:07:49
Oleh : Andina Pertiwi - 141424003 & Anggun Islamagesvi - 141424004 (andinapertiwi23@gmail.com)
Dibuat : 2018-09-25, dengan 4 file

Keyword : Komposit, serat eceng gondok, asetilasi, karbon
Subjek : Composite, water hyacinth fiber, acetylation, carbon

Penggunaan kayu yang berlebihan untuk kebutuhan manusia dapat menyebabkan kerusakan pada alam. Solusi untuk masalah ini adalah dengan membuat material baru yang memiliki sifat seperti kayu dari bahan lain seperti komposit. Bahan komposit yang digunakan yaitu resin poliester, karbon dan serat eceng gondok karena eceng gondok dianggap sebagai gulma perairan dan memiliki kandungan serat 20% berat. Tujuan dari penelitian ialah menentukan komposisi terbaik antara serat, karbon dan resin poliester pada komposit, serta pengaruh serat terasetilasi pada kekuatan mekanik komposit. Komposit dibuat dengan metode hand lay-up dengan variasi fraksi volume serat eceng gondok, karbon, dan resin. Spesimen untuk uji tarik mengacu kepada ASTM D638-02A. Asetilasi serat eceng gondok digunakan untuk meningkatkan sifat hidrofobik serat dengan dilakukan variasi komposisi reaktan asam asetat glasial dan asam asetat anhidrat terhadap serat. Pengujian kadar asetil serat mengacu pada ASTM D871-96. Asetilasi serat terbaik diperoleh dengan perbandingan massa serat : asam asetat glacial : asam asetat anhidrat adalah 1: 21 :21,6 dengan temperatur operasi 120oC dalam waktu reaksi 2 jam. Komposisi komposit terbaik dipilih berdasarkan kedekatan nilai sifat mekanik komposit dengan kayu pinus sebagai rujukan adalah 25% volume serat eceng gondok terasetilasi, 25% volume karbon dan 50% volume resin dengan kekuatan tarik 51,97% lebih kecil dari kayu pinus, modulus Young 57,58% lebih kecil dari kayu pinus, dan elongasi 6,637% lebih besar dari kayu pinus. Kata Kunci: Komposit, serat eceng gondok, asetilasi, karbon.

Deskripsi Alternatif :

Excessive use of wood for human needs can cause damage to nature. The solution of this problem is to create new materials that have properties like wood from other materials such as composites. Composite materials that used are carbon and water hyacinth fiber because water hyacinth is parasite and has a fiber content of 20% by weight. The purpose of this study is determine the best variation of composition between fiber, carbon,and polyester resin, and the effect of acetylated fibers on composite mechanical strength. The matrix used is polyester resin with MEKPO hardener. The composite is made by hand lay-up method with variation of volume hyacinth fiber, carbon, and resin. Specimen test for clarity test against ASTM D638-02A. Acetylation of water hyacinth fibers was used to improve the hydrophobic properties of the fibers by varying the composition of glacial acetic acid acetic acid and anhydrous acetic acid to fiber, to test acetyl content based on ASTM D871-96. Acetylation that choosen of mass ratio between fiber : glacial acetic acid : anhydrous acetic acid is 1:21:21,6 with an operating temperature of 120oC and 2 hour reaction time. The best composite compositions selected based on the proximity value of composite mechanical properties with pine wood as a reference is 25% by volume of the acetylated hyacinth fiber, 25% carbon volume and 50% resin volume with tensile strength 51.97% smaller than pine wood, Young modulus, 58% smaller than pine wood, and elongation 6.637% bigger than pine wood. Keywords: Composite, water hyacinth fiber, acetylation, carbon.

Beri Komentar ?#(0) | Bookmark

PropertiNilai Properti
ID PublisherJBPTPPOLBAN
Organisasi
Nama KontakHelmi Purwanti
AlamatJl. Trsn. Gegerkalong Hilir Ds. Ciwaruga
KotaBandung
DaerahJawa Barat
NegaraIndonesia
Telepon022 201 3789 ext. 168, 169, 239
Fax022 201 3889
E-mail Administratorhelmi.purwanti@polban.ac.id
E-mail CKOhelmi.purwanti@polban.ac.id

Print ...

Kontributor...

  • Pembimbing 1: Ir. Ninik Lintang, M.Sc.

    Pembimbing 2: Dra. Endang Widiastuti, M.Si. , Editor: Erlin Arvelina

Download...