Pembuatan dan Karakterisasi Half Cell (Elektrolit+Anoda) Solid Oxide Fuel Cell (SOFC)

Fabrication and Characterization of Half Cell (Electrolyte+Anode) Solid Oxide Fuel Cell (SOFC)

Tugas Akhir, 003 / 2020 / ANK
Undergraduate Theses from JBPTPPOLBAN / 2021-08-23 12:03:23
Oleh : Atikah Halimah Putri - 171431004 & Depi Rapika - 171431006 (atikah.halimah.anki17@polban.ac.id)
Dibuat : 2021-08-23, dengan 4 file

Keyword : Half cell SOFC, Vickers hardness, sintering, tape-casting, porosity.
Subjek : Half cell SOFC, kekerasan Vickers, sintering, tape-casting, porositas.

Kemajuan teknologi di era globalisasi memberikan manfaat di berbagai aspek, salah satunya teknologi fuel cell yang dapat memberikan solusi dalam penyediaan listrik masa depan. Salah satu teknologi sel bahan bakar yang mempunyai prospek yang baik adalah SOFC (Solid Oxide Fuel Cell). SOFC mengubah bahan bakar menjadi listrik secara langsung melalui reaksi elektrokimia, bekerja pada suhu 550-850oC sehingga berpeluang untuk internal dry reforming. Dalam penelitian ini, dibuat sistem half cell (elektrolit+anoda) SOFC dengan metode aqueous tape casting sebagai kelanjutan dari pembuatan anoda pada penelitian sebelumnya. Bubur anoda dan elektrolit dibuat dengan mencampurkan bahan baku yaitu NiO, YSZ (Yttria-stabilized zirconia), PEG (polyethylene glycol), PVA (polyvinyl alcohol), gliserol, dan air demineral. Penggilingan campuran menggunakan mesin ball mill dengan variasi waktu 12 jam dan 24 jam. Selanjutnya penghilangan gelembung udara (gas), pencetakan (tape-casting), pengeringan pada suhu ruang, sintering pada suhu 1200oC, dan karakterisasi lempengan anoda dan half cell SOFC. Hasil karakterisasi anoda dan half cell menggunakan SEM/EDX menunjukkan morfologi lempengan anoda dengan pori berkisar 300 nm – 1000 nm. Komposisi lempengan anoda menunjukkan kadar 14-23% Ni, 46-52% Zr, dan 7% Y, sedangkan elektrolit terdiri dari 50-51% Zr dan 7-9% Y. Kekerasan Vickers lapisan elektrolit berkisar pada 254-261 HV dan anoda berkisar pada 194-196 HV. Porositas anoda dengan menggunakan metode Archimedes menunjukkan angka 11% volume. Dalam rencana pengukuran komposisi gas hasil dry reforming telah diidentifikasi keperluan penambahan gas sample valve TRACE 1300 pada alat GC (Gas Chromatography) dan penyediaan campuran gas standar untuk membuat kurva kalibrasi, dengan kolom kapiler dan detector TCD (Thermal Conductivity Detector).

Deskripsi Alternatif :

The rapid development of technology in global era provides benefits in various aspects of life, one of them is fuel cell technology which offers solutions for future needs of electricity. SOFC (Solid Oxide Fuel Cell) is one of fuel cell technology that can directly convert fuel into electricity through electrochemical reactions. These SOFCs work at 550-850oC which allows for internal reforming reactions to occur at the anode. In this research, half cell (electrolyte+anode) SOFCs were made by aqueous tape casting method. Anode and electrolyte slurry was prepared by mixing raw materials NiO, YSZ (Yttria-stabilized zirconia), PEG (polyethylene glycol), PVA (polyvinyl alcohol), glyserol in demineralized water. The slurry was ball milled for 12 hour and 24 hours. Then, the slurry was degassed, aqueous tape cast, dried at room temperature, sintered at 1200 oC, and characterized. SEM/EDX results showed that the anode pore size ranging from 300 to 1000 nm and the anode showing 14-23% Ni, 46-52% Zr, and 7% Y, while the electrolyte showing 50-51% Zr and 7-9% Y. The Vickers Hardness obtained were 254-261 HV and 194-196 HV for the electrolyte and anode layer respectively. Using Archimedes test method the anode showed 11% pore volume. The plan for GC (Gas Chromatography) analysis of dry reforming product gases on the anode as catalyst is to install a TRACE 1300 gas sample valve and utilize a standard gas mixture to produce calibration curves, while using a GC capillary column and a TCD (Thermal Conductivity Detector).

Beri Komentar ?#(0) | Bookmark

PropertiNilai Properti
ID PublisherJBPTPPOLBAN
Organisasi
Nama KontakHelmi Purwanti
AlamatJl. Trsn. Gegerkalong Hilir Ds. Ciwaruga
KotaBandung
DaerahJawa Barat
NegaraIndonesia
Telepon022 201 3789 ext. 168, 169, 239
Fax022 201 3889
E-mail Administratorhelmi.purwanti@polban.ac.id
E-mail CKOhelmi.purwanti@polban.ac.id

Print ...

Kontributor...

  • Pembimbing 1: Lina Troskialina, B.Sc., M.Sc., Ph.D.




    Pembimbing 2: Riniati, S.Pd., M.Si., Editor: Muhammad Abdillah Islamy, S.Pd

Download...