Pembuatan Zeolit Y Menggunakan Sumber Silika Dan Alumina Dari Limbah Sintesis Zeolit Y

Production Of Zeolite Y Using Source Of Silica And Alumina From Synthesis Zeolite Y Wastes

Skripsi, 008 / 2018 / KPB
Undergraduate Theses from JBPTPPOLBAN / 2018-09-25 12:20:00
Oleh : Desi Bentang Widiyanti - 141424009 & Ghina Fauziyyah - 141424014 (desibentangwidiyanti@gmail.com; ghinfauziyyah@gmail.com)
Dibuat : 2018-09-25, dengan 4 file

Keyword : Mother liquor, zeolit Y, starting material, sintesis hidrotermal
Subjek : Mother liquor, zeolite Y, starting material, hydrothermal synthesis

Perkembangan industri di Indonesia saat ini berlangsung dengan baik terutama industri pengolahan minyak dengan proses FCC (fluid catalytic cracking) dan proses hydrocracking. Kebutuhan katalis berdasarkan Pertamina (2011) untuk FCC sebesar 27-30 ton/hari sedangkan hydrocracking sebesar 380 ton/tahun. Salah satu komponen utama katalis untuk proses FCC dan hydrocracking adalah zeolit Y. Oleh karena itu pembuatan zeolit Y penting demi memenuhi kebutuhan katalis bagi kedua proses tersebut. Penelitian tugas akhir ini bertujuan untuk membuat zeolit Y dari mother liquor hasil sintesis zeolit Y. Mother liquor mengandung SiO2 dan Al2O3 yang dapat berperan sebagai komponen utama pembentukan zeolit Y, oleh karenanya dalam penelitian ini mother liquor digunakan sebagai bahan baku sintesis zeolit Y. Metode sintesis zeolit Y yang dilakukan adalah secara hidrotermal menggunakan bibit kristal lynde tipe Y, dan formulasi starting material SiO2/Al2O3 = 10; Na2O/Al2O3 = 13-15 dan H2O/Al2O3 = 896-1060 dengan waktu sintesis selama 8-23 jam. Sebelum sintesis diperlukan pematangan starting material pada suhu kamar selama 11 jam. Prosedur sintesis zeolit Y yang telah dikembangkan menghasilkan zeolit dengan rasio SiO2/Al2O3 yaitu 2,91, kristalinitas 71,9% pada waktu sintesis 11 jam dengan formulasi starting material 13,38Na2O : Al2O3 : 10,41SiO2 : 895,87H2O. Hasil tersebut membuktikan bahwa mother liquor masih dapat digunakan kembali sebagai bahan baku sintesis zeolit Y. Berdasarkan penelitian ini diketahui bahwa waktu sintesis zeolit Y diatas 19 jam mengindikasikan terbentuknya senyawa selain zeolit Y dikarenakan adanya reaksi konsekutif. Didapatkan pula kecenderungan perubahan kualitas produk zeolit Y yang dipengaruhi oleh konsentrasi komponen-komponen dalam starting material pada rasio SiO2/Al2O3 yang sama. Kata Kunci: Mother liquor, zeolit Y, starting material, sintesis hidrotermal.

Deskripsi Alternatif :

The development of industry in Indonesia is currently underway with the oil processing industry especially well with the process of FCC (fluid catalytic cracking) and hydrocracking process. Necessity of catalyst based on Pertamina (2011) for the FCC of 27-30 tonnes/day while hydrocracking of 380 tonnes/year. One of the main components of catalyst for FCC and hydrocracking process is zeolit Y. Therefore making zeolits Y are important to meet the needs of the catalyst for both these processes. This research of final project aims to make the zeolit Y from mother liquor as side product of zeolit Y synthesis. Mother liquor containing SiO2 and Al2O3 which can act as a main component of the formation of zeolit Y, therefore in this study mother liquor used as a raw material for the synthesis of zeolit Y. The method of zeolit Y synthesis is generally done with hydrothermal using crystal seed lynde type Y, and starting material formulations are SiO2/Al2O3 = 10; Na2O/Al2O3 = 13-15 and H2O/Al2O3 = 896-1060 with a time of synthesis for 8-23 hours. Before the synthesis necessary to do aging of starting material at room temperature for 12 hours. The zeolit Y synthesis procedures that have been developed produce zeolits with SiO2/Al2O3 ratios that is 2.91, crystallinity 71.9% at the time of the synthesis of 11 hours with starting formulations material 13.38Na2O: 10.41SiO2: Al2O3: 895.87H2O. The results prove that mother liquor can still be reused as raw material for the synthesis of zeolit Y. Based on these studies it is known that the time of the synthesis of zeolite Y above 19 hours indicates the formation of compounds other than zeolite Y due of consecutive reactions. There is also obtained the tendency of changes in product quality of zeolite Y that is affected by the concentration of the components in the starting material at the same ratio of SiO2/Al2O3. Keywords: Mother liquor, zeolite Y, starting material, hydrothermal synthesis.

Beri Komentar ?#(0) | Bookmark

PropertiNilai Properti
ID PublisherJBPTPPOLBAN
Organisasi
Nama KontakHelmi Purwanti
AlamatJl. Trsn. Gegerkalong Hilir Ds. Ciwaruga
KotaBandung
DaerahJawa Barat
NegaraIndonesia
Telepon022 201 3789 ext. 168, 169, 239
Fax022 201 3889
E-mail Administratorhelmi.purwanti@polban.ac.id
E-mail CKOhelmi.purwanti@polban.ac.id

Print ...

Kontributor...

  • Pembimbing: Dr. Ir. Endang Sri Rahayu, M.T., Editor: Erlin Arvelina

Download...