Pengujian Tanpa Merusak Pada Sambungan Las Pelat Baja Menggunakan Metode Ultrasonik Berdasarkan Prosedur American Welding Society

Non-Destructive Testing on Steel Plate Weld Joints Using Ultrasonic Methods Based on American Welding Society Procedures

Tugas Akhir, 001 / 2018 / AE-GMF
Undergraduate Theses from JBPTPPOLBAN / 2018-10-09 14:07:35
Oleh : Fikri Aulia Izzatur Rahim - 151229001 (fikriaultur29.fa@gmail.com)
Dibuat : 2018-10-09, dengan 4 file

Keyword : NDT, Ultrasonik, AWS, Las, Baja
Subjek : NDT, Ultrasonic, AWS, Weld, Steel

Kekuatan struktur material pada sambungan las pelat baja akan berkurang dan menyebabkan fatigue yang dapat disebabkan oleh proses pengelasan. Untuk mencegah hal tersebut diperlukan Non-Destructive Test (NDT). Non-destructive Test adalah salah satu teknik mencari retak atau cacat pada sebuah spesimen tanpa merusak spesimen tersebut. Salah satu metode NDT adalah ultrasonik yang menggunakan gelombang suara frekuensi tinggi yang dipancarkan kedalam spesimen uji dan dipantulkan kembali ke alat uji. Untuk mendapatkan hasil yang maksimal dan sesuai standar, pengujian dilakukan berdasarkan prosedur American Welding Society (AWS). Prosedur pertama yang harus dilakukan adalah melakukan kalibrasi probe normal dan probe sudut, seperti kalibrasi sensitifitas, resolusi, range, dan penentuan titik index probe. Kemudian mencatat nilai dB saat kalibrasi sensitifitas lubang 1.5 mm pada blok V1 sebagai reference level untuk dibandingkan dengan dB dari cacat yang ada pada spesimen. Setelah prosedur kalibrasi selesai, pengujian dapat dilakukan. Hasil pengujian pada las sambungan pelat baja terdapat cacat berupa lack of fusion. Menurut acceptance criteria AWS, seluruh cacat termauk ke dalam kategori kelas A yaitu cacat besar dan harus di-reject. Kata kunci: NDT, Ultrasonik, AWS, Las, Baja.

Deskripsi Alternatif :

The strength of the material structure of the steel plate welded joints will be reduced and fatigue can be caused by the welding process. To prevent this, it is necessary Non-destructive Test (NDT). Non-destructive Test is one technique of finding cracks or defects in a specimen without damaging the specimen. One of NDT method is ultrasonic that uses high-frequency sound waves emitted into test specimens and is reflected back to the test apparatus. To obtain maximum results and standards, the tests are performed according to the American Welding Society (AWS) procedures. The first procedure to perform is to perform normal probe calibration and angle probe calibration, such as sensitivity calibration, resolution, range, and probe point index determination. Then records the dB value when calibrating the 1.5 mm hole sensitivity on block V1 as the reference level for comparison with dB of defects in the specimen. After the calibration procedure is complete, testing can be performed. Test results on welded steel plate joints is defective lack of fusion. According to AWS acceptance criteria, all defects included in class A and it means are large defects and must be rejected. Keywords: NDT, Ultrasonic, AWS, Weld, Steel.

Beri Komentar ?#(0) | Bookmark

PropertiNilai Properti
ID PublisherJBPTPPOLBAN
Organisasi
Nama KontakHelmi Purwanti
AlamatJl. Trsn. Gegerkalong Hilir Ds. Ciwaruga
KotaBandung
DaerahJawa Barat
NegaraIndonesia
Telepon022 201 3789 ext. 168, 169, 239
Fax022 201 3889
E-mail Administratorhelmi.purwanti@polban.ac.id
E-mail CKOhelmi.purwanti@polban.ac.id

Print ...

Kontributor...

  • Pembimbing: Mochammad Luthfi, Dipl.Ing., M.T., M.Sc., Editor: Erlin Arvelina

Download...