Karakterisasi Membran Hibrid Komposit Nafion/Silika untuk Aplikasi Baterai Aliran Redoks (RFB)

Characterization of Nafion/Silica Hybrid Composite Membranes for Redox Flow Battery (RFB) Applications

Advanced Materials Research Vol. 911 (2014) pp 45-49.
Journal from JBPTPPOLBAN / 2015-02-03 08:03:35
Oleh : Haryadi; Y. B. Gunawan; S.P. Mursid; D. Haryogi (haryadi@polban.ac.id)
Dibuat : 2015-02-03, dengan 1 file

Keyword : Nafion, Silica, sol-gel
Url : http://10.4028/www.scientific.net/AMR.911.45

Membran hibrid Nafion/Silika dibuat melalui metoda insitu sol-gel untuk sistem baterai aliran redoks. Dalam penelitian ini membran baru Nanokomposit hibrid Nafion/silika organik termodifikasi dibuat melalui reaksi insitu sol-gel untuk campuran tetraethoxysilane (TEOS) dan trimethoxyprohanthiol (TMSP). Sifat-sifat utama membran hibrid Nafion/Silika ini diukur dan dibandingkan dengan membran Nafion dan Nafion/Silika. Analisis spektrum FTIR dari membran hibrid menyatakan bahwa fasa silika dan silika organik termodifikasi terbentuk dengan baik didalam membran hibrid tersebut. Hasil dari pengukuran XRD menunjukkan bahwa membran hibrid Nafion ini tidak dipengaruhi oleh partikel SiO2. Membran Hibid Nafion/Silika ini meunujkkan nilai kapasitas penukar ion yang mendekati sama dengan membran orisinal Nafion-117 yang tidak dimodifikasi. Kandungan air yang berada didalam membran hibrid Nafion/Silika menunjukkan penurunan yang sangat besar dibandingkan dengan membran orisinal Nafion-117 yang berarti rendahnya pelintasan air (water cross over) yang banyak dihadapi kendalanya pada aplikasi baterai aliran redoks (RFB)

Deskripsi Alternatif :

Nafion/Silica hybrid membranes were prepared via in situ sol–gel method for redox flow battery (RFB) system. In this work, a novel Nafion/organically modified silicate hybrids nanocomposite membrane was prepared via in situ sol–gel reactions for mixtures of tetraethoxysilane (TEOS) and trimethoxyprohanthiol (TMSP). The primary properties of Nafion/Silica hybrids membrane were measured and compared with Nafion and Nafion/SiO2 hybrid membranes. Fourier transform infrared spectra (FT-IR) analysis of the hybrids membranes reveal that the silica and organic modified silica phase is well formed within hybrids membrane. The XRD results indicate thatthe Nafionhybrid membranes are not influenced by SiO2 nanoparticles. Nafion/Silica hybrid membrane shows nearly the same ion exchange capacity (IEC)and slightly greater of proton conductivity as pristine Nafion-117 membrane. The water uptake for Nafion/Organosilica hybrids membrane shows greatly reduced than a pristine Nafion 117,suggesting of low water cross over that is mostly faced in the RFB applications.

Beri Komentar ?#(0) | Bookmark

PropertiNilai Properti
ID PublisherJBPTPPOLBAN
Organisasi
Nama KontakHelmi Purwanti
AlamatJl. Trsn. Gegerkalong Hilir Ds. Ciwaruga
KotaBandung
DaerahJawa Barat
NegaraIndonesia
Telepon022 201 3789 ext. 168, 169, 239
Fax022 201 3889
E-mail Administratorhelmi.purwanti@polban.ac.id
E-mail CKOhelmi.purwanti@polban.ac.id

Print ...

Kontributor...

  • , Editor: Idayu Gemalia

Download...