Pengaruh Variabel Panjang Ukur Batang Uji Tarik Terhadap Sifat Mekanik pada Baja Beton Polos

Effect of Gage Length Variable of Specimen on Mechanical Properties of Steel Reinforcing Bars

Journal from JBPTPPOLBAN / 2014-04-03 11:40:56
Oleh : Muhamad (ptmebdg@gmail.com)
Dibuat : 2014-04-03, dengan 1 file

Keyword : Uji tarik, spesimen, kekuatan tarik, perpanjangan, panjang ukur

Penelitian ini bertujuan mempelajari pengaruh variabel panjang ukur batang uji (spesimen) baja beton polos pada uji tarik terhadap sifat-sifat mekanik material yaitu kekuatan tarik maksimum, kekuatan luluh, kekuatan patah, modulus elastisitas, perpanjangan dan pengurangan diameter. Pada pengujian bahan terutama uji tarik, direkomendasikan menggunakan batang uji proposional sesuai dengan ISO 82-1974(E), Karena berbagai alasan, dalam praktek sering dijumpai pengujian bahan tidak dapat memenuhi standar batang uji proposional yang telah direkomendasikan. Penggunaan spesimen tidak standar ini kemungkinan akan mempengaruhi hasil uji. Untuk mengetahui pengaruh spesimen yang tidak standar dilakukan penelitian secara eksperimen melalui uji tarik pada material baja beton polos dengan diameter uji 10 mm dan pajang ukur batang uji bervariasi. Pengujian tarik dilakukan dengan mesin uji tarik yang dilengkapi dengan system akuisisi data dan perangkat lunak untuk pengolahan data hasil uji tarik. Hasil eksperimen menunjukan bahwa panjang ukur batang uji pada baja beton polos tidak memberikan pengaruh yang signifikan terhadap sifat-sifat mekanik material kecuali pada perpanjangan dan pengurangan penampang. Semakin besar perbandingan antara panjang ukur batang uji dengan diameter nominalnya maka semakin menurun nilai perpanjangan (elongation) dan pengurangan penampang (reduction area).

Deskripsi Alternatif :

This research aims to study the effect of gage length variable of rod test (specimen) of steel reinforcing bars in tensile test againts the mechanical properties of the material (the maximum tensile strength , yield strength , fracture strength , elastic modulus , elongation and reduction in diameter). In materials testing especially tensile test , it is recommended to use a proportional test rod according to ISO 82-1974 (E), For various reasons , often encountered in practice of material test can not meet the standard test bars have proportionately recommended. The use of non-standard specimens is likely to affect the test results. To determine the effect of non-standard specimens in experimental research conducted through tensile test on steel reinforcing bars material with a diameter of 10 mm and a kind of gage length. Tensile testing machine tensile testing is done by the system is equipped with a data acquisition and data processing software for the tensile test results. The experimental results showed that the gage length of the rod test on steel reinforcing bars does not have a significant influence on the mechanical properties of the material except for the elongation and reduction in cross-section . The greater the ratio between the gage length of the specimen to the nominal diameter decreases the value of the elongation and a reduction in cross-section.

Beri Komentar ?#(3) | Bookmark

PropertiNilai Properti
ID PublisherJBPTPPOLBAN
Organisasi
Nama KontakHelmi Purwanti
AlamatJl. Trsn. Gegerkalong Hilir Ds. Ciwaruga
KotaBandung
DaerahJawa Barat
NegaraIndonesia
Telepon022 201 3789 ext. 168, 169, 239
Fax022 201 3889
E-mail Administratorhelmi.purwanti@polban.ac.id
E-mail CKOhelmi.purwanti@polban.ac.id

Print ...

Kontributor...

  • , Editor: Idayu Gemalia

Download...