PENGARUH PENAMBAHAN ABU LIMBAH SISA PEMBAKARAN ALUMINIUM TERHADAP SIFAT MORTAR

THE INFLUENCE OF ADDING WASTE ASH OF ALUMUNIUM COMBUSTION TO THE MORTAR PROPERTIES

Tugas Akhir, 014 / 2012 / KGE
Undergraduate Theses from JBPTPPOLBAN / 2015-11-18 09:21:21
Oleh : Muhammad Nur Hafidz - 091111047 & Teten - 091111055
Dibuat : 2012-11-26, dengan 4 file

Keyword : mortar, abu aluminium,flow, waktu ikat, kuat tekan, penyerapan air dan perubahan panjang
Subjek : mortar, aluminium ash, flow, belt timing, compressive strength, water absorption, and the change length

Mortar adalah adukan yang terdiri dari pasir, bahan perekat, dan air. Campuran antara bahan-bahan tersebut menggunakan perbandingan tertentu sehingga didapatkan nilai kuat tekan yang maksimal. Perlua danya pengembangan teknologi dibidang mortar yang menghasilkan kualitas mortar lebih baik. Salahsatu teknik pengembangan tersebut maka perlu adanya bahan pengganti atau bahan tambah material mortar untuk meningkatkan kualitas mortar yang baik dan ekonomis. Bahan tambah yang dapat digunakan harus mengandung senyawa silika dan kandungan kimia lainnya.Abu limbah sisa pembakaran Aluminium merupakan material yang memiliki kandungan silika dan kimia lain didalamnya. Kajian ini dilakukan untuk mengetahui pengaruh penambahan abu aluminium terhadap sifat-sifat mortar dengan prosentase 0%,2%,4%,6%,8%dan10% dari berat semen, baik mortar segar maupun mortar keras. Metodologi dalam penelitian ini adalah, uji pendahuluan, persiapan peralatan dan bahan yang digunakan, pengujian bahan-bahan yang digunakan pada campuran mortar yang terdiri dari semen, pasir dan abu aluminium sesuai dengan SNI, perancangan campuran mortar dengan perbandingan 1 PC : 3 PS dengan variasi campuran abu aluminium 0%, 2%, 4%, 6%, 8% dan10% terhadap berat semen, pencampuran dan pengadukan mortar, pengujian mortar segar yang terdiri dari pengujian flow dan waktu ikat, pembuatan benda uji mortar dan dilakukan perawatan sampai umur 28 hari, pengujian mortar keras yang terdiri dari uji kuat tekan, penyerapan air dan perubahan panjang, analisa hasil pengujian pada mortar segar serta mortar keras, evaluasi hasil pengujian dan kesimpulan.Hasil pengujian menunjukan bahwa penambahan prosentase abu aluminium meningkatkan tingkat kekentalan mortar dan memperlambat waktu ikat mortar, menurunkan nilai kuat tekan dan terjadi perubahan panjang.Variasi campuran dengan penambahan abu aluminium 2%, 6%, 8% dan 10% masuk kedalam mortar type N (SNI 03-6882-2002), karena pada umur 28 hari kuat tekan mortar melebihi kuat tekan rata-rata yang disyaratkan dalam spesifikasi mortar type N yaitu 5,2 MPa. Sedangkan pada penambahan abu aluminium 0% dan 4% masuk kedalam mortar type S (SNI 03-6882-2002), karena pada umur 28 hari kuat tekan mortar melebihi kuat tekan rata-rata yang disyaratkan dalam spesifikasi mortar type Syaitu12,4 MPa.Ditinjau dari pengujian kuat tekan mortar, penyerapan air dan perubahan panjang pada umur 28 hari, penambahan abu aluminium 4% adalah paling optimal dibandingkan dengan penambahan abu aluminium 2%, 6%, 8%, dan 10%. Kata kunci: mortar, abu aluminium,flow, waktu ikat, kuat tekan, penyerapan air dan perubahan panjang.

Deskripsi Alternatif :

Mortar is a mixture consisting of adhesives, sand and water. The mixtures of these components use a particular ratio to obtain the maximum value of compressive strength. In this case, the development of technology is definitely necessary in order to produce better mortar. One of the innovations that should be used is the change of the ingredients or the addition of new components in making better mortar that more economic than it was before. The additional components that can be used must consist of silica compounds and the other contents of chemical material. Alumunium waste ash from the combustion is a material that contains silica and other chemicals for instance. The study was conducted to determine the effects of the addition of alumunium ash toward the characteristics of mortar with a percentage of 0%, 2%, 4%, 6%, 8% and 10% by weight of cement, both fresh mortar and hard mortar. The methodology in this study is a preliminary test, preparation of equipment and materials used, testing of materials used in mortar mix consisting of cement, sand and alumunium ash according to the SNI, designing of mortar mixed with a ratio of 1 PC : 3 PS mixed with the combination of alumunium ash 0%,2%,4%,6%,8% and 10% of the weight of cement, blending and mixing mortar, testing of fresh mortar consisting of flow and timing belt testing, making mortar specimens and performed the treatment until the age of 28 days, testing of hard mortar consisting of testing of compressive strength , water absorption and the change in length, analyzing of test result on fresh mortar and hard mortar, evaluating of the test result and making the conclusion. The result test shows that the addition of alumunium ash percentage increases viscosity and slows the belt mortar, lowers the value of compressive strength and changes the length. The variation of mixture with the addition of alumunium ash 2%,6%,8% and 10% into mortar type N (SNI 03-6882-2002), because at the age of 28 days the mortar compressive strength exceeds the average of compressive strength required in the specification of type N mortar is 5,2 MPa. While the addition of alumunium ash 0% and 4% is categorized the mortar type S (SNI 03-6882-2002) because at the age of 28 days the mortar compressive strength exceeds the average of compressive strength required in the specification of type S mortar is 12,4 MPa. Considering from the mortar compressive strength testing, water absorption and the change in length at the age of 28 days the addition of alumunium ash 4% is more optimal than the addition of aluminium ash 2%, 6%, 8%, dan 10%.


Key words: mortar, aluminium ash, flow, belt timing, compressive strength, water absorption, and the change length.

Beri Komentar ?#(0) | Bookmark

PropertiNilai Properti
ID PublisherJBPTPPOLBAN
Organisasi
Nama KontakHelmi Purwanti
AlamatJl. Trsn. Gegerkalong Hilir Ds. Ciwaruga
KotaBandung
DaerahJawa Barat
NegaraIndonesia
Telepon022 201 3789 ext. 168, 169, 239
Fax022 201 3889
E-mail Administratorhelmi.purwanti@polban.ac.id
E-mail CKOhelmi.purwanti@polban.ac.id

Print ...

Kontributor...

  • Pembimbing : Nursyafril, ST., SP1. , Editor: Erlin Arvelina

Download...