Recovery Alumina (Al2O3) dari Coal Fly Ash (CFA) menjadi Polyaluminum Chloride (PAC)

Recovery of Alumina (AL2O3) from Coal Fly Ash (CFA) to Produce Polyaluminum Chloride (PAC)

Journal from JBPTPPOLBAN / 2012-07-25 16:08:48
Oleh : Ninik Lintang Edi Wahyuni (niniklintang@yahoo.com)
Dibuat : 2012-07-25, dengan 1 file

Keyword : alumina, coal fly ash (CFA), polyaluminum chloride (PAC)

Coal fly ash (CFA) adalah limbah sisa pembakaran batubara yang termasuk ke dalam bahan beracun dan berbahaya (B3). Penelitian ini dimaksudkan untuk memanfaatkan alumina (Al2O3) yang terkandung dalam CFA menjadi produk polyaluminum chloride (PAC), yaitu bahan koagulan yang mempunyai nilai ekonomi cukup tinggi. Proses preparasi PAC dari CFA merupakan modifikasi dari metode Park (1997) untuk membuat PAC dari tanah liat, karena komposisi bahan baku yang hampir sama. Proses preparasi meliputi leaching, kristalisasi, dekomposisi parsial, pelarutan dalam air, serta sentrifugasi. Leaching dilakukan pada temperatur 105 oC, dan waktu optimum yang diperoleh adalah 60 menit, yang memberikan persen recovery sebesar 41,2%. Untuk proses dekomposisi parsial diperoleh temperatur optimum 200 oC dan waktu optimum 200 menit, yang memberikan yield total 18,76 %. Uji kinerja terhadap produk PAC yang diperoleh dilakukan dengan metode Jar Test, dan dosis optimumnya adalah 761,6 ppm yang mampu menurunkan kekeruhan air limbah artificial dari 123,3 NTU menjadi 4,68 NTU.

Deskripsi Alternatif :

Coal fly ash (CFA) is a waste generated by coal-fired boiler, and is categorized as hazardous waste. This research aims to utilize alumina (Al2O3) content of CFA to produce polyaluminum chloride (PAC)-a type of coagulant that has relatively high economic value. Preparation of PAC from CFA was a modification of Park’s method (1997) that produce PAC from clay due to composition similarities of raw materials. The preparation processes were leaching, crystalization, partial decomposition, water dilution, and centrifugation. Leaching of alumina from fly ash was carried out at temperature of 105oC, which gave optimum time of 60 minutes, and percent recovery of 41.2%. For partial decomposition process, the optimum temperature of 200oC and optimum time of 200 minutes gave total yield of 18.76%. Performance test of produced PAC was conducted by jar test method, which gave optimum dose of 761.6 ppm to reduce turbidity of artificial waste water from 123.3 NTU to 4.68 NTU.

Beri Komentar ?#(0) | Bookmark

PropertiNilai Properti
ID PublisherJBPTPPOLBAN
Organisasi
Nama KontakHelmi Purwanti
AlamatJl. Trsn. Gegerkalong Hilir Ds. Ciwaruga
KotaBandung
DaerahJawa Barat
NegaraIndonesia
Telepon022 201 3789 ext. 168, 169, 239
Fax022 201 3889
E-mail Administratorhelmi.purwanti@polban.ac.id
E-mail CKOhelmi.purwanti@polban.ac.id

Print ...

Kontributor...

  • , Editor: Idayu Gemalia

Download...