The Effect of Hydrazines Concentration and Time on Corrosion Rate of Carbon Steel in Heat Exchanger

Tugas Akhir, 006 / 2018 / JTK
Undergraduate Theses from JBPTPPOLBAN / 2019-02-06 09:18:31
Oleh : 151411005 - Dani Gustiana Sandie - 151411056 - Ridhwan Rais (ridhwan.rais.tkim15@polban.ac.id)
Dibuat : 2019-02-06, dengan 4 file

Keyword : Effect of Hydrazines, Concentration, Time, Corrosion Rate, Carbon Steel, Heat Exchanger
Subjek : Konsentrasi Inhibitor, Hydrazine, Waktu , Laju Korosi, Baja Karbon,Heat Exchanger

Korosi dapat terjadi secara lebih cepat di dalam double pipe heat exchanger. Pipa bagian dalam adalah bagian yang paling rawan terjadi korosi, karena terdapat dua jenis zat cair yang mengalir baik di dalam maupun di luar pipa tersebut. Inhibitor korosi berupa hydrazine dapat menurunkan laju korosi pada pipa, sehingga umur pipa di dalam alat penukar panas tersebut dapat bertahan lebih lama. Tujuan dari dilakukannya penelitian ini adalah untuk mengetahui laju korosi pada pipa di dalam double pipe heat exchanger baik sebelum dan sesudah penambahan hydrazine. Dalam penelitian ini terdapat beberapa kondisi operasi seperti laju alir larutan garam sebagai masukan pada pipa bagian dalam sebesar 74,7 liter per jam, suhu air panas pada pipa bagian luar sebesar 50 sampai 55ºC, waktu pengukuran pada rentang 0 - 20 jam (0 jam;4 jam;8 jam;12 jam;16 jam;20 jam), dan konsentrasi hydrazine yang ditambahkan pada rentang 0,3% - 0,9% (0,3%;0,6%;0,9%). Korosi yang terjadi diamati berdasarkan perhitungan laju korosi dengan menggunakan metode kehilangan massa. Hasil penelitian menunjukkan bahwa laju korosi pada pipa yang dialiri larutan garam tanpa penambahan inhibitor sebesar 171,891 mpy, sedangkan laju korosi pada pipa yang dialiri larutan garam dan ditambahkan inhibitor hydrazine dengan konsentrasi berturut-turut (0,3%,0,6%,0,9%) adalah sebesar (62,615 mpy;48,569 mpy;6,938 mpy), serta efisiensi inhibitor yang diperoleh pada waktu 4 jam pengujian berdasarkan konsentrasi hydrazine yang sudah disebutkan adalah sebesar (63,5%;71,74%;95,96%). Dari ketiga konsentrasi tersebut, diperoleh hasil bahwa konsentrasi hydrazine terbaik yaitu pada konsentrasi 0,9% yang menghasilkan laju korosi paling rendah yaitu sebesar 6,983 mpy.

Deskripsi Alternatif :

Corrosion can occur more quickly in double pipe heat exchanger. The pipe (tube) is the most vulnerable part of corrosion, because there are two types of liquid that flow both inside and outside the pipe. Hydrazine as inhibitor of corrosion can reduce the corrosion rate in the pipe and make it lasts longer when it's being used in heat exchanger. The aim of this research is to determine the corrosion rate of the pipe in double pipe heat exchanger before and after the addition of hydrazine. In this research, there are several operating conditions such as the flow rate of saline solution as input to the tube section pipe is 74.7 liters per hour, the temperature of the hot water in the shell section pipe is 50 to 55ºC, the range of time is 0-20 hours (0 hours; 4 hours, 8 hours, 12 hours, 16 hours, 20 hours), and the concentration of hydrazine that has been added is in the range of 0.3% - 0.9% (0.3%; 0.6%; 0.9%). Corrosion that observed is based on the calculation of corrosion rate using the weight loss method. Results show that the corrosion rate on the pipes flowed with saline solution without the addition of inhibitors is 171,891 mpy, while the corrosion rates on the pipes flowed with saline solution and added with hydrazine inhibitors with consecutive concentrations (0.3%, 0 , 6%, 0.9%) are (62,615 mpy; 48,569 mpy; 6,938 mpy), and then, for inhibitor efficiencies that obtained at 4 hours by using hydrazine at the same concentration above are (63,5%;71,74%;95,96%) . And finally, the result shows that the best concentration of hydrazine to be added in saline solution is at 0,9%, which obtaines the lowest corrosion rate, 6,893 mpy.

Beri Komentar ?#(0) | Bookmark

Properti	Nilai Properti
ID Publisher	JBPTPPOLBAN
Organisasi
Nama Kontak	Erlin Arvelina
Alamat	Jl. Trsn. Gegerkalong Hilir Ds. Ciwaruga
Kota	Bandung
Daerah	Jawa Barat
Negara	Indonesia
Telepon	022 201 3789 ext. 168, 169, 239
Fax	022 201 3889
E-mail Administrator	erlin.arvelina@polban.ac.id
E-mail CKO	erlin.arvelina@polban.ac.id