Photodegradation of Synthetic Dyes Using TiO2-Zeolite Nanocomposites

Tugas Akhir, 018 / 2018 / TKI
Undergraduate Theses from JBPTPPOLBAN / 2019-02-07 14:20:23
Oleh : 151411034 - Alqizza L. H. - 151411037 - Azka M. S (alqizzalukmannul@gmail.com)
Dibuat : 2019-02-07, dengan 4 file

Keyword : Photocatilytic, Nanocomposite, TiO2, Zeolite, and Skycion Yellow HE 4R.
Subjek : Fotokatilitik, Nanokomposit, TiO2, Zeolit, dan Skycion Yellow HE 4R.

Telah dilakukan penelitian fotodegradasi zat warna limbah cair buatan menggunakan metode fotokatalitik dengan penambahan nanokomposit TiO2 – zeolit. Tujuan penelitian ini untuk menentukan rasio massa TiO2 - zeolit terbaik dalam proses degradasi zat warna Skycion Yellow HE 4R dan karakterisasi nanokomposit dengan uji Scanning Electron Microscpoy (SEM) dan Electron Dispersive X-Ray Spectroscopy. Zeolit alam diaktivasi terlebih dahulu sebelum dikompositkan dengan TiO2. Perbandingan TiO2 – zeolit yang digunakan pada pembuatan nanokomposit adalah 20:80, 40:60, 50:50, dan 60:40. Percobaan pendahuluan dilakukan dengan menggunakan limbah cair buatan Skycion Yellow HE 4R. Pada perbandingan TiO2 : zeolit 40 : 60 didapatkan degradasi zat warna sebesar 67%. Karakterisasi motfologi menggunakan SEM (Scanning Electron Microscopy), analisis komposisi menggunakan EDS (Electron Different X-Ray Spectroscopy), analisis warna menggunakan spektrofotometri UV-VIS, dan analisis (Chemical Oxygen Demand) COD.

Deskripsi Alternatif :

Photodegradation of artificial liquid wastes has been carried out using photocatalytic method by adding TiO2 - zeolite nanocomposite. The purpose of this study was to determine the best mass ratio of TiO2 - zeolite in the degradation process of Skycion Yellow HE 4R dyestuff and nanocomposite characterization by Microscpoy Electron Scanning (SEM) and Electron Dispersive X-Ray Spectroscopy. Natural zeolite is activated before being composted with TiO2. The ratio of TiO2 - zeolite used in the manufacture of nanocomposites is 20:80, 40:60, 50:50, and 60:40. Preliminary experiments were carried out using liquid waste made by Skycion Yellow HE 4R. In the comparison of TiO2: zeolite 40: 60, dye degradation was 67%. Characterization of motology using SEM (Scanning Electron Microscopy), composition analysis using EDS (Electron Different X-Ray Spectroscopy), color analysis using UV-VIS spectrophotometry, and COD analysis (Chemical Oxygen Demand)

Beri Komentar ?#(0) | Bookmark

Properti	Nilai Properti
ID Publisher	JBPTPPOLBAN
Organisasi
Nama Kontak	Erlin Arvelina
Alamat	Jl. Trsn. Gegerkalong Hilir Ds. Ciwaruga
Kota	Bandung
Daerah	Jawa Barat
Negara	Indonesia
Telepon	022 201 3789 ext. 168, 169, 239
Fax	022 201 3889
E-mail Administrator	erlin.arvelina@polban.ac.id
E-mail CKO	erlin.arvelina@polban.ac.id