Utilization of Goethe Plant Leaves as Corrosion Inhibitor of Carbon Steel In HCl Solution

Tugas Akhir, 021 / 2018 / TKI
Undergraduate Theses from JBPTPPOLBAN / 2019-02-07 14:41:16
Oleh : 151411039 - Fadil Hardian - 151411045 - Ilham Januari (deal.dingbading@gmail.com)
Dibuat : 2019-02-07, dengan 4 file

Keyword : Utilization, Goethe Plant Leaves,Corrosion Inhibitor, Carbon Steel, HCl Solution
Subjek : Ekstrak, Cocor Bebek, Inhibitor Korosi, Baja Karbon, Larutan Asam Klorida

Daun cocor bebek (Kalanchoe pinnata) memiliki kandungan antioksidan diantaranya adalah tanin dan flavanoid yang dapat dimanfaatkan sebagai inhibitor korosi baja karbon dalam lingkungan HCl. Penelitian ini bertujuan untuk mengkaji pengaruh ekstrak menggunakan pelarut polar dan semi polar sebagai inhibitor korosi. Daun cocor bebek dimaserasi menggunakan pelarut metanol, yang selanjutnya diekstraksi dengan pelarut n-heksan, aseton, dan etil asetat. Ekstrak daun cocor bebek diuji kromatografi lapis tipis dan uji korosi dengan variasi kosentrasi 50, 100, 200, 400, 800, 1600 ppm dan waktu 12, 24, 36, 48, 60 jam. Hasil penelitian menunjukkan bahwa ekstrak cocor bebek sebesar 24,54 gram yang mengandung senyawa antioksidan seperti tanin dan flavonoid yang dengan larutan FeCl3 berwarna hijau kehitaman dan uji Kromatografi Lapis Tipis menunjukkan warna kuning. Uji ekstrak sebagai inhibitor korosi ditunjukkan bahwa waktu pengkorosian mempengaruhi laju korosi baja karbon dalam larutan HCl dengan laju korosi terendah dicapai pada waktu 60 jam dengan konsentrasi ekstrak dalam pelarut etil asetat 1600 ppm mampu menurunkan laju korosi menjadi 21,03 mpy dengan efisiensi inhibisi 65,08%. Untuk ekstrak dalam pelarut aseton menunjukkan laju korosi baja karbon dalam larutan HCl 0,1 M lebih rendah dalam pelarut heksan dan etil asetat dengan laju korosi 27,60 mpy pada konsentrasi 1600 ppm dengan efisiensi 81,51%. Ekstrak dalam pelarut aseton di lingkungan HCl 0,1M menunjukan lebih efektif dibandingan dalam HCl 0,5 M, konsentrasi optimum ekstrak dalam menginhibisi baja karbon dalam larutan HCl 0,1 M adalah 400 ppm dengan laju korosi 40,04 mpy dengan efisiensi 73,17%.

Deskripsi Alternatif :

Goethe plant (Kalanchoe pinnata) contains antioxidants such as tannins and flavonoids that can be utilized as carbon steel corrosion inhibitors in an HCl environment. This study aims to examine the effect of extract using polar and semi-polar solvents as corrosion inhibitors. Goethe leaves are macerated using a methanol solvent, which is subsequently extracted with n-hexane, acetone, and ethyl acetate. Goethe leaves extract was tested by thin layer chromatography and corrosion test with concentration variation 50, 100, 200, 400, 800, 1600 ppm and time 12, 24, 36, 48, 60 hours. The results showed that the extract of goethe leaves for 24.54 grams containing antioxidant compounds such as tannins and flavonoids with blackish-green FeCl3 solution and TLC test showed yellow color. Extracting tests of various corrosion inhibitors showed that time of corrosion affects the corrosion rate of carbon steel in HCl solution with the lowest corrosion rate achieved at 60 hours with the concentration of extract in 1600 ppm ethyl acetate having reduced corrosion rate of 21.03 mpy with an inhibitory efficiency of 65.08 %. For the extract in acetone solvent the corrosion rate of carbon steel in 0.1 M HCl solution was compared in the hexane and ethyl acetate solvents. The condition of the lowest corrosion rate was achieved at a corrosion rate of 27.60 mpy at a concentration of 1600 ppm. The results of the extract in acetic solvent in the 0.1M HCl environment showed more effective than HCl 0.5 M with an inhibitory efficiency of 81.51%. The optimum concentration of extract in inhibiting carbon steel in 0.1 M HCl solution was 400 ppm with a corrosion rate of 40.04 mpy with an efficiency of 73.17%.

Beri Komentar ?#(0) | Bookmark

Properti	Nilai Properti
ID Publisher	JBPTPPOLBAN
Organisasi
Nama Kontak	Erlin Arvelina
Alamat	Jl. Trsn. Gegerkalong Hilir Ds. Ciwaruga
Kota	Bandung
Daerah	Jawa Barat
Negara	Indonesia
Telepon	022 201 3789 ext. 168, 169, 239
Fax	022 201 3889
E-mail Administrator	erlin.arvelina@polban.ac.id
E-mail CKO	erlin.arvelina@polban.ac.id