The Effect of Processing Time and Zinc Concentration as a Layer Between Nickel - Chrome and Chrome Electroplating Processes on Aluminium Metal

Tugas Akhir, 024 / 2018 / TKI
Undergraduate Theses from JBPTPPOLBAN / 2019-02-08 13:38:17
Oleh : 151411042 - Fuad Hilmy mahdy - 151411051 - Muhamad Faizal (isal12_1239@yahoo.com)
Dibuat : 2019-02-08, dengan 4 file

Keyword : Electroplating, nickel-chrome, chrome, zinkat process, time process, concentration
Subjek : Elektroplating, nikel-krom,krom, proses zinkat, waktu proses, konsentras

Elektroplating nikel-krom dan krom pada logam aluminium adalah metoda pelapisan untuk meningkatkan sifat mekanik logam yang akan dilapis dengan memanfaatkan arus listrik searah. Elektroplating pada alumunium membutuhkan lapisan antara yang dapat dihasilkan untuk meningkatkan daya rekat lapisan nikel-krom dan krom.Lapisan antara menggunakan zinkat sebagai pre-treatment. Penelitian ini bertujuan menentukan waktu proses zinkat dan konsentrasi zinkat serta membandingkan produk elektroplating nikel-krom dan krom melalui uji tebal lapisan, kekerasan dan daya rekat. Elektroplating nikel menggunakan larutan nikel sulfat dengan rapat arus 4.3 A/dm2pada suhu 45 0C dan elektroplating krom menggunakan larutan krom sulfat dengan rapat arus 20 A/dm2 pada suhu 60 0C. Variasi pre-treatment yaitu pada konsentrasi zinkat 2.5 %; 5 %; 7.5 %; 10 %; 12.5 % dan waktu proses zinkat adalah 15 detik; 30 detik; 45 detik. Proses elektroplating nikel-krom yaitu proses elektroplating nikel dilanjutkan elektroplating krom. Waktu proses pada elektroplating nikel-krom yaitu elektroplating nikel 15 menit dan elektroplating krom 15 menit sedangkan elektroplating krom dilakukan selama 15 menit. Hasil elektroplating nikel-krom menghasilkan lapisan terbaik pada waktu proses zinkat 45 detik dan konsentrasi zinkat 7.5 % dengan tebal lapisan nikel 48.8 μm dan krom 26.5 μm sedangkan elektroplating krom dicapai pada waktu proses zinkat 45 detik dan konsentrasi zinkat 2.5 % dengan tebal lapisan krom 21.69 μm dan mempunyai daya rekat yang baik. Lapisan nikel-krom mempunyai ketebalan dan daya rekat yang lebih baik daripada lapisan krom pada logam aluminium.

Deskripsi Alternatif :

Nickel-chrome and chrome electroplating in aluminum metal is a coating method to improve the mechanical properties of metals to be coated by utilizing direct electric current. Electroplating on aluminum requires an intermediate layer which can be generated to improve the adhesion of the nickel-chrome and chromium layers. The intermediate layer uses zinc as a pre-treatment. This study aims to determine the time zinkat process and zinc concentration and compare the nickel-chrome and chrome electroplating products through thickness of the coating, hardness and adhesion.Electroplating nickel using a solution of nickel sulfate with a current density of 4.3 A / dm2 at a temperature of 45 0C and chrome electroplating using a solution of chromium sulfate with a current density of 20 A / dm2 at a temperature of 60 0C. Pre-treatment variation is at concentration zinkat 2.5%; 5%; 7.5%; 10%; 12.5% and time zinkat process is 15 seconds; 30 seconds; 45 seconds. The process of nickel-chrome electroplating is the process of nickel electroplating followed by chrome electroplating. The processing time for nickel-chrome electroplating is 15 minutes of nickel electroplating and 15 minutes of chrome electroplating while chrome electroplating is carried out for 15 minutes. The results of nickel-chrome electroplating produced the best coating during zinkat process 45 seconds and zinkat concentration 7.5% with nickel thin layer 48.8 μm and chromium 26.5 μm while chrome electroplating was achieved during zinkat process 45 seconds and zinkat concentration 2.5% with chrome surface layer 21.69 μm and has good adhesion. The nickel-chrome layer has a better thickness and adhesion than the chrome coating on the aluminum metal.

Beri Komentar ?#(0) | Bookmark

Properti	Nilai Properti
ID Publisher	JBPTPPOLBAN
Organisasi
Nama Kontak	Erlin Arvelina
Alamat	Jl. Trsn. Gegerkalong Hilir Ds. Ciwaruga
Kota	Bandung
Daerah	Jawa Barat
Negara	Indonesia
Telepon	022 201 3789 ext. 168, 169, 239
Fax	022 201 3889
E-mail Administrator	erlin.arvelina@polban.ac.id
E-mail CKO	erlin.arvelina@polban.ac.id