C-Dots, Fotokatalis, Water Splitting, Gas Hidrogen.

Tugas Akhir, 030 / 2018 / TKI
Undergraduate Theses from JBPTPPOLBAN / 2019-02-11 14:25:16
Oleh : 151411055 - Reza Fitrayana - 151411060 - Sunsun Sugianto (sugiantosunsun97@gmail.com)
Dibuat : 2019-02-11, dengan 4 file

Keyword : C-Dots, Photocatalyst , Water Splitting, Hydrogen Gas
Subjek : C-Dots, Fotokatalis, Water Splitting, Gas Hidrogen.

Energi terbarukan (renewable energy) menjadi sumber energi alternatif yang menjanjikan untuk dimanfaatkan menjadi bahan bakar yang ramah lingkungan. Gas hidrogen muncul sebagai energi ramah lingkungan yang dapat dihasilkan melalui proses steam reforming, elektrolisis dan water splitting. Penelitian ini bertujuan untuk melakukan Kajian Awal Produksi Gas Hidrogen dengan Metode Fotokatalitik Menggunakan C-Dots dari Ampas Aren sebagai Fotokatalis. Penelitian ini dilakukan melalui beberapa tahap, yaitu pretreatment ampas aren, pembuatan C-Dots, penggabungan C-Dots dan ZnO nanopartikel (80-100nm) sebagai cocatalyst, serta proses water splitting. Pembuatan fotokatalis C-Dots terbaik dihasilkan pada suhu karbonisasi 225oC selama 2 jam dan ekstraksi C-Dots dilakukan dengan menggunakan microwave pada temperatur 68oC selama 40 menit. Hasil dari karbonisasi dan ekstraksi C-Dots dianalisis menggunakan alat FTIR, spektrofotometer UV-Vis, sinar UV (366 nm) dan Transmition Electrone Microscope (TEM low resulotion). Hasil karakterisasi FTIR menunjukan gugus fungsional karakteristik dari C-Dots, hasil dari spektrum UV-Vis menunjukan eksitasi C-Dots pada 288 nm serta karakteristik fotoluminensi dibawah sinar UV. Morfologi C-Dots dari hasil TEM menunjukan ukuran partikel dalam rentang 3-8 nm dengan distribusi ukuran partikel dominan 5 nm (36,67%). Pada proses water splitting dilakukan variasi rasio fotokatalis C-Dots dan cocatalyst 1:5 ; 2:5 ; 3:5 dengan waktu proses selama 10 jam pada suhu pemanasan fotoreaktor 60oC. Gas hidrogen hasil proses water splitting dianalisis menggunakan Gas Chromatohgraphy menunjukan kuantitas gas hidrogen yang dihasilkan dengan variasi yang dilakukan menunjukan hasil terbaik 0,002% (v/v) hidrogen.

Deskripsi Alternatif :

Renewable energy is a promising alternative energy to be used for environmentally friendly fuel. Hydrogen gas emerge as an environmentally friendly energy that can be generated through steam reforming, electrolysis, and water splitting process. This study aims to conduct an initial study of hydrogen gas production through a process of water splitting with photocatalytic method using C-Dots of palm waste/dregs as a photocatalyst. This research is done through several stages, namely pretreatment of palm waste, making C-Dots, merging C-Dots and ZnO nanoparticles (80-100nm) as cocatalyst, and water splitting process. The best photocatalyst C Dots is produced at 225oC carbonization temperature for 2 hours and C-Dots extraction was carried out by microwave at 68oC for 40 minutes. The results of carbonization and C-Dots extraction were analyzed using FTIR, spectrophotometer UV-Vis, UV light (366 nm) and Transmission Electrone Microscope (TEM low resulotion). The FTIR characterization results show the characteristic functional groups of C-Dots, the results of the UV-Vis spectrum show the C-Dots excitation at 288 nm and the photoluminant characteristics under UV light. Morphology C-Dots of TEM results shows particle size in the range of 3-8 nm with a dominant particle size distribution of 5 nm (36,67%). In the process of water splitting is done by ratio variation of C-Dots and cocatalyst 1:5 ;2:5; 3:5 (w/w) with processing time for 10 hours and photoreactor heating temperature of 60°C. The hydrogen gas from the water splitting process was analyzed using Chromatohgraphy Gas showing the quantity of hydrogen gas produced by the variation performed showed the best result of 0,002% (v/v) hydrogen.

Beri Komentar ?#(0) | Bookmark

Properti	Nilai Properti
ID Publisher	JBPTPPOLBAN
Organisasi
Nama Kontak	Erlin Arvelina
Alamat	Jl. Trsn. Gegerkalong Hilir Ds. Ciwaruga
Kota	Bandung
Daerah	Jawa Barat
Negara	Indonesia
Telepon	022 201 3789 ext. 168, 169, 239
Fax	022 201 3889
E-mail Administrator	erlin.arvelina@polban.ac.id
E-mail CKO	erlin.arvelina@polban.ac.id