SYNTHESIS AND CHARACTERIZATION OF NICKEL MOLYBDENUM CATALYST SUPPORTED ON GAMMA ALUMINIUM OXIDE FOR DIESEL OIL HYDROTREATING

Tugas Akhir, 009 / 2012 / ANK
Undergraduate Theses from JBPTPPOLBAN / 2013-11-08 09:22:58
Oleh : Agung Apriansyah - 091431001 & Kiki Maryam - 091431016
Dibuat : 2013-09-30, dengan 4 file

Keyword : hydrotreating, impregnasi, katalis hydrotreating, penyangga, karakterisasi
Subjek : hydrotreating, impregnation, hydrotreating catalyst, support, characterization

Katalis NiMo/ γ-Al2O3 disintesis dengan metode impegnasi basah menggunakan katapal sebagai sumber aluminium oksida, nikel sebagai prekursor, dan molibdenum sebagai promotor. Proses sintesis meliputi pembuatan penyangga, kalsinasi penyangga, impregnasi, dan kalsinasi katalis. Penelitian ini bertujuan untuk mendapatkan katalis NiMo/ γ-Al2O3 yang mempunyai kualitas terbaik berdasarkan hasil karakterisasinya sehingga didapatkan S120316A2 sebagai formula terbaik. Katalis tersebut selanjutnya akan diaplikasikan di unit hydrotreating minyak diesel. Karakterisasi yang dilakukan meliputi kekuatan mekanik, analisis termogravimetri (TGA), dan analisis adsorpsi-desorpsi nitrogen untuk menentukan luas permukaan, ukuran pori, dan volume pori. Metode pengujian yang dilakukan mengacu pada ASTM D 4179-01 (kekuatan mekanik), ASTM D 3663-03 (luas permukaan), ASTM D 4641-94 (ukuran pori), dan ASTM D 4222-03 (volume pori). Hasil pengujian kekuatan mekanik sampel memperlihatkan bahwa S120316A2 mempunyai nilai kekuatan mekanik terbesar yaitu 6,89 kg. Peningkatan konsentrasi asam nitrat sampai 7 % dan penurunan garam posfat menyebabkan kekuatan mekanik semakin besar. Hasil TGA penyangga menunjukkan bahwa penyangga aluminium oksida terdekomposisi sempurna dan terbentuk fasa gamma terjadi saat mendekati temperatur 550oC. Hasil analisis adsorpsi-desorpsi nitrogen menunjukkan bahwa jenis pori penyangga dan katalis yang telah dibuat merupakan jenis mesopori (diameter 2-50 nm). Luas permukaan, ukuran pori, dan volume pori S120316A2 sebagai penyangga hasil sintesis terbaik secara berturut-turut adalah 272 m2/g, 73 Å, dan 0,50 cc/g. Kata kunci : hydrotreating, impregnasi, katalis hydrotreating, penyangga, karakterisasi.

Deskripsi Alternatif :

Catalyst NiMo/ γ-Al2O3 was synthesized by wet impregnation methode with catapal as aluminium oxide source, nickel as precursor, and molybdenum as promotor. The synthesis process includes synthesis of supports, calcination of supports, impregnation, and calcination of catalysts. The research is aimed to obtain the best catalyst NiMo/ γ-Al2O3 based on characterization results, thus obtained S120316A2 as the best formula and then it is applied in hydrotreating unit for diesel oil. The characterization includes crushing strength, thermogravimetric analysis (TGA), and nitrogen adsorption-desorption analysis for determining surface area, pore size, and pore volume. The testing methods refer to ASTM D 4179-01 (crushing strength), ASTM D 3663-03 (surface area), ASTM D 4641-94 (pore size), and ASTM D 4222-03 (pore volume). The analysis of samples showed that S120316A2 is the highest crushing strength of 6,89 kg. The increasing of nitrate acid concentration until 7 % and reduction of lead phosphate salt produced the highest crushing strength. The thermogravimetric analysis showed that aluminium oxide supports completely decomposed and formed the gamma phase occurred at 550oC. The adsorption-desorption nitrogen showed that pore type of synthesized support and catalyst is mesopori type (diameter 2-50 nm). Surface area, pore size, and pore volume of S120316A2 as the best support are 272 m2/g, 73 Å, and 0,50 cc/g respectively. Keywords : hydrotreating, impregnation, hydrotreating catalyst, support, characterization.

Beri Komentar ?#(0) | Bookmark

Properti	Nilai Properti
ID Publisher	JBPTPPOLBAN
Organisasi
Nama Kontak	Erlin Arvelina
Alamat	Jl. Trsn. Gegerkalong Hilir Ds. Ciwaruga
Kota	Bandung
Daerah	Jawa Barat
Negara	Indonesia
Telepon	022 201 3789 ext. 168, 169, 239
Fax	022 201 3889
E-mail Administrator	erlin.arvelina@polban.ac.id
E-mail CKO	erlin.arvelina@polban.ac.id