The Effect of Zeolite NaY Synthesis Process Condition from Kaolin Belitung as a Raw Material on The Quality of Zeolite HY Modification Product

Tugas Akhir, 003 / 2018 / TKI
Undergraduate Theses from JBPTPPOLBAN / 2018-10-16 09:12:03
Oleh : Alvin Maulana - 151411002 & Septian Hardi Prasetya - 151411027 (septian.hardip@gmail.com)
Dibuat : 2018-10-16, dengan 4 file

Keyword : Zeolite Y, katalis hydrocracking, kaolin, sintesis hidrotermal,
Subjek : Y Zeolite, Hydrocracking Catalyst, Kaolin, Hydrothermal Synthesis

Zeolit HY adalah komponen penyusun katalis Hydrocracking sebagai penyedia fasa aktif asam yang dapat disintesis dengan bahan baku utama yang mengandung SiO2 dan Al2O3. Bahan baku yang menyediakan sumber SiO2 dan Al2O3 dapat berasal dari bahan sintetik maupun bahan alam seperti kaolin. Telah banyak penelitian yang mengkaji tentang potensi kaolin sebagai bahan baku zeolite Y. Murrat (1992) menyatakan bahwa rasio molar SiO2/Al2O3 antara 7-10 dalam leached metakaolin merupakan rasio yang dapat mendukung terbentuknya Zeolite Y. Imanuddin (2017) yang berhasil mengkonversi kaolin menjadi zeolite NaY dengan menggunakan dosis bibit kristal 2 resep dan waktu sintesis 15 jam. Tujuan dari penelitian ini adalah untuk mengetahui pengaruh rasio SiO2/Al2O3 dalam leached metakaolin sebagai bahan baku, pengaruh dosis bibit kristal serta waktu sintesis terhadap kualitas hasil modifikasi zeolit NaY menjadi zeolit HY dan mendapatkan kondisi proses yang tepat agar memperoleh zeolite NaY dengan rasio SiO2/Al2O3≥2,7 dan zeolit HY yang memiliki kandungan Na<1%. Penelitian ini melalui beberapa tahap proses, yaitu aktivasi kaolin menjadi metakaolin, dealuminasi metakaolin, sintesis hidrotermal zeolit NaY, dan modifikasi zeolit NaY menjadi zeolit HY. Produk yang diperoleh dilakukan uji karakteristik kristalinitas dengan XRD, karakteristik morfologi dengan SEM, struktur pori dengan Surface Area and Pore Size Analyzer dan kadar SiO2, Al2O3 dan Na dengan AAS. Hasil penelitian menunjukkan bahwa kondisi operasi yang tepat untuk menghasilkan zeolite NaY yang memiliki rasio SiO2/Al2O3 2,88 adalah dengan leached metakaolin dengan rasio SiO2/Al2O3 5,65; 5%-b padatan dalam starting material; dosis bibit kristal 4 resep dengan sintesis zeolit NaY secara hidrotermal selama 18 jam dan didapatkan hasil modifikasi zeolite HY dengan kadar Na <1%-b. Kata Kunci: Zeolite Y, katalis hydrocracking, kaolin, sintesis hidrotermal.

Deskripsi Alternatif :

HY Zeolite is a constituent component of Hydrocracking catalyst as a provider of acid active phase which can be synthesized with the main raw material containing SiO2 and Al2O3. Raw materials that provide sources of SiO2 and Al2O3 can come from synthetic materials or natural materials such as kaolin. There have been many studies examining about the potential of kaolin as a raw material for zeolite Y. Murrat (1992) states that the molar ratio of SiO2/ Al2O3 between 7-10 in leached metakaolin is a ratio that can support the formation of Zeolite Y. Imanuddin (2017) which successfully converts kaolin into zeolite NaY by using a 2 recipe for crystal seeds and 15 hours of synthesis time. The purpose of this study was to determine the effect of the ratio of SiO2 / Al2O3 in leached metakaolin as raw material, the effect of crystal seed dose and synthesis time on the quality of modified NaY zeolite to HY zeolite and get the right process conditions to obtain zeolite NaY with SiO2/Al2O3 ratio≥2.7 and HY zeolite which has Na <1%-w. This research went through several stages of the process, activation of kaolin to metakaolin, dealumination of metakaolin, synthesis of zeolite NaY hydrothermal, and modification of NaY zeolite to zeolite HY. The product obtained was tested for the characteristics of crystallinity with XRD, morphological characteristics with SEM, pore structure with Surface Area and Pore Size Analyzer and concentration of SiO2, Al2O3 and Na with AAS. The results showed that the proper operating conditions to produce zeolite NaY which has a ratio of SiO2/Al2O3 2,88 is with leached metakaolin with a molar ratio of SiO2/Al2O3 5,65; 5%-w solids in starting material; and 4 recipe for crystal seed by synthesizing NaY zeolite hydrothermally for 18 hours and getting zeolite HY modification with Na <1% -w. Keywords: Y Zeolite, Hydrocracking Catalyst, Kaolin, Hydrothermal Synthesis.

Beri Komentar ?#(0) | Bookmark

Properti	Nilai Properti
ID Publisher	JBPTPPOLBAN
Organisasi
Nama Kontak	Erlin Arvelina
Alamat	Jl. Trsn. Gegerkalong Hilir Ds. Ciwaruga
Kota	Bandung
Daerah	Jawa Barat
Negara	Indonesia
Telepon	022 201 3789 ext. 168, 169, 239
Fax	022 201 3889
E-mail Administrator	erlin.arvelina@polban.ac.id
E-mail CKO	erlin.arvelina@polban.ac.id