Design and Manufacturing of Powder Metallurgy Generating Tool with Gas Argon Atomizing Media

Tugas Akhir, 019 / 2013 / TME
Undergraduate Theses from JBPTPPOLBAN / 2017-03-22 11:37:44
Oleh : Amrullah - 101211036 & Irvan Ardy Wiguna - 101211049 (amrullah739@gmail.com; vand_a2@yahoo.co.id)
Dibuat : 2017-03-22, dengan 4 file

Keyword : Powder metallurgy, chamber, nozzle, atomisasi, dan fabrikasi
Subjek : Powder metallurgy, chamber, nozzle, atomization, and fabrication

Teknologi Metalurgi serbuk (Powder Metallurgy ; P/M) telah digunakan untuk membuat produk yang relatif sulit diproses dengan cara pemesinan. Selain itu, berbagai literatur melaporkan keunggulan teknologi metallurgy serbuk yang terbukti mampu memproduksi suatu produk dengan harga yang relatif rendah dengan kualitas yang lebih baik. Modal utama proses produksi dengan rute ini adalah serbuk logam yang dibuat dengan berbagai metoda baik secara mekanik, kimiawi, dan atomisasi. Tujuan dibuatnya alat ini di antaranya untuk menghasilkan serbuk logam yang sesuai standar dan diharapkan dapat mengetahui secara jelas bentuk dan proses pembuatannya. Dalam Tugas Akhir ini difokuskan pada proses produksi serbuk logam dengan metode atomisasi dengan media gas Argon, untuk memecah sekaligus pembekuan logam cair dengan menambahkan chamber air sebagai penampungnya. Secara umum digambarkan tahap pelaksanaan yang meliputi perancangan nozzle dan ruang atomisasi, fabrikasi peralatan atomisasi serta pengujian dengan logam yang titik leburnya dibawah 1000oC seperti pada Alumunium. Hasil dari pembuatan alat ini berupa serbuk logam Al yang sudah memenuhi standar, yaitu diameternya <100µm. Dan bentuk dari serbuk logam yang telah dihasilkan dari proses atomisasi dengan gas Argon memperlihatkan bentuk partikel yang berbeda-beda dari serbuk logam Al ada yang berbentuk bulat (Spherical) ,bercabang (dendritic) ,bersudut (angular), dan bentuk yang tidak beraturan (irregular). Kata kunci: Powder metallurgy, chamber, nozzle, atomisasi, dan fabrikasi.

Deskripsi Alternatif :

Powder metallurgy technology (Powder Metallurgy, P / M) has been used to make a product that is poorly processed by machining. In addition, the literature reported advantages of powder metallurgy technology that proved capable of producing a product with a relatively low price with better quality. Major capital production process with metal powders routes are created with a variety of methods, both mechanical, chemical, and atomization. The purpose of the tool in which to produce metal powders that are standards compliant and are expected to know clearly the form and the manufacturing process. In this final project is focused on the production of metal powders by atomization method with argon gas media, to break up at the same time by adding molten metal freezing chamber as water reservoirs. In general, the illustrated that the implementation phase includes the design of the nozzle and atomization chamber, atomizing equipment fabrication and testing of the metal below the melting point of 1000oC as in aluminum. Result of this tool in the form of Al metal powders that already meet the standards, the diameter <100 µm. And shape of the metal powder that has been generated from argon gas atomization process to show the form of different particles of metal powder Al exist in the form of spherical, dendritic, angular, and irregular. Keywords: Powder metallurgy, chamber, nozzle, atomization, and fabrication.

Beri Komentar ?#(0) | Bookmark

Properti	Nilai Properti
ID Publisher	JBPTPPOLBAN
Organisasi
Nama Kontak	Erlin Arvelina
Alamat	Jl. Trsn. Gegerkalong Hilir Ds. Ciwaruga
Kota	Bandung
Daerah	Jawa Barat
Negara	Indonesia
Telepon	022 201 3789 ext. 168, 169, 239
Fax	022 201 3889
E-mail Administrator	erlin.arvelina@polban.ac.id
E-mail CKO	erlin.arvelina@polban.ac.id