Recondition and Modification of Flame Harden Machine

Tugas Akhir, 025 / 2013 / TME
Undergraduate Theses from JBPTPPOLBAN / 2017-03-22 15:20:57
Oleh : Armiya Farhana - 101211003 & F. Yudhi Mandraguna - 101211012 (army_gituuu@yahoo.com; fauzanyudhimandraguna@yahoo.com)
Dibuat : 2017-03-22, dengan 4 file

Keyword : Flame Harden, Rekondisi , Kekerasan
Subjek : Flame Harden, Recondition , Hardness

Pemilihan material adalah suatu hal yang penting. Setiap material dan logam memliki karakteristiknya masing-masing, namun untuk logam yang sama dapat saja memiliki sifat yang berbeda. Sifat logam berkaitan erat dengan struktur mikro. Salah satu cara merubahnya adalah dengan heat treatment. Mesin Flame Harden merupakan salah satu alat yang dapat digunakan untuk melakukan proses heat treatment, khususnya untuk pengerasan permukaan material. Pelaksanaan rekondisi ini meliputi pemeriksaan kondisi mesin pada setiap komponennya, perbaikan serta penggantian komponen yang telah rusak atau sudah tidak ada. Uji kekerasan yang dihasilkan dari proses surface hardening dan uji kedalaman pengerasan dilakukan setelah rekondisi selesai. Setelah dilakukan rekondisi, setiap komponen pada mesin Flame Harden dapat berfungsi kembali dan digunakan untuk kegiatan praktikum. Dari hasil pengujian kekerasan sampel, menggunakan mesin yang telah di rekondisi, didapat hasil kekerasan 30 HRC sampai 45 HRC. Kata kunci: Flame Harden, Rekondisi , Kekerasan.

Deskripsi Alternatif :

The choice of material is an important thing. Every material and metal posses certain characteristics, but the same metal may have different properties. Metal properties are closely related to their micro structure. One way to change it is by heat treatment. The Flame Harden machine is one of the tools that can be used to perform the heat treatment process, especially for hardening the surface of a material The reconditioning process includes checking the condition of each engine component, repair, and replacement of components that have been damaged or subside. Hardness test that resulted from the surface hardening process and depth test was conducted after reconditioning completed. After reconditioning was completed, each component of the Flame Harden machine can continue to function and be used for practical activities. From the sample's hardness test, using the reconditioned machine, hardness results obtained was 30 HRC to 45 HRC Keyword: Flame Harden, Recondition , Hardness.

Beri Komentar ?#(0) | Bookmark

Properti	Nilai Properti
ID Publisher	JBPTPPOLBAN
Organisasi
Nama Kontak	Erlin Arvelina
Alamat	Jl. Trsn. Gegerkalong Hilir Ds. Ciwaruga
Kota	Bandung
Daerah	Jawa Barat
Negara	Indonesia
Telepon	022 201 3789 ext. 168, 169, 239
Fax	022 201 3889
E-mail Administrator	erlin.arvelina@polban.ac.id
E-mail CKO	erlin.arvelina@polban.ac.id