Literature Study of Utilization of Breadfruit Stem (Artocarpus Altilis) as a Coating For Nanomagnetite (Fe3O4) in Reduction of Chromium (Cr) Metal in Wastewater

Tugas Akhir, 005 / 2021 / TKI
Undergraduate Theses from JBPTPPOLBAN / 2024-01-09 11:57:28
Oleh : Aziz Alfiansyah - 181411009 & Choizar Alwi - 181411010 (choizar.alwi.tki18@polban.ac.id )
Dibuat : 2024-01-09, dengan 4 file

Keyword : breadfruit stems, cellulose, Fe3O4 nanoparticles, coating, chromium
Subjek : batang sukun, selulosa, nanopartikel Fe3O4, coating, kromium

Kajian ini mempelajari potensi selulosa dari batang sukun (Artocarpus artilis) dengan kandungan 53,58% selulosa untuk dijadikan coating pada nanopartikel Fe3O4. Sintesis nanopartikel Fe3O4 dinilai efektif untuk dilakukan menggunakan metode kopresipitasi karena sederhana dan murah dalam biaya operasionalnya. Beberapa faktor yang mempengaruhi sintesis nanopartikel Fe3O4 adalah penggunaan garam besi, kekuatan ionik, pH, laju pengadukan, temperatur, serta rasio ion ferri dan ferro untuk mengoptimalkan ukuran serta morfologinya. Berdasarkan faktor tersebut diperoleh hasil kajian berupa garam besi yang digunakan adalah FeSO4.7H2O dan Fe2(SO4)3 dengan kekuatan ionik tertinggi. Rasio ion ferri dan ferro yang digunakan adalah 2:1 sesuai perbandingan stoikiometri. Suasa pH media larutan optimum pada pH 11 dengan laju pengadukan 900 rpm. Perolehan α-selulosa dari batang sukun menggunakan pre-treatment alkali dinilai efektif dalam menghilangkan lignin dan melarutkan kandungan jenis selulosa lain seperti β-selulosa dan ϒ-selulosa sehingga diperoleh kandungan α-selulosa dengan kemurnian tinggi. Tahapan lanjut menggunakan proses bleaching untuk membantu menghilangkan sisa lignin sehingga dapat memutihkan produk α-selulosa. Diharapkan perolehan α-selulosa dari batang sukun berkisar pada kemurnian 70-80%. Pelapis α-selulosa dapat menurunkan ukuran nanopartikel Fe3O4 dalam mencegah terjadinya aglomerasi dan menjadi matriks bagi nanopartikel Fe3O4 dalam membentuk nanokomposit sehingga dapat meningkatkan kapasitas adsorpsi dalam menurunkan kadar logam kromium (Cr) pada air limbah.

Deskripsi Alternatif :

This study determines the potential of cellulose from breadfruit stems (Artocarpus artilis) with 53.58% cellulose content to be used as a coating on Fe3O4 nanoparticles. The synthesis of Fe3O4 nanoparticles is considered effective to be carried out using the coprecipitation method because it is simple and inexpensive in operational costs. Several factors that influence the synthesis of Fe3O4 nanoparticles are the use of iron salts, ionic strength, pH, stirring rate, temperature, and the ratio of ferric and ferrous ions to optimize size and morphology. Based on these factors, the results of the study in the form of iron salts used were FeSO4.7H2O and Fe2(SO4)3 with the highest ionic strength. The ratio of ferric and ferrous ions used is 2:1 according to the stoichiometric ratio. The optimum pH of the solution medium at pH 11 with a stirring rate of 900 rpm. Obtaining α-cellulose from breadfruit stems using alkaline pre-treatment is considered effective in removing lignin and dissolving other cellulose content such as β-cellulose and ϒ-cellulose in order to obtain high-purity α-cellulose content. The next stage uses a bleaching process to help remove residual lignin so that it can make a cellulose product. It is expected that the yield of α-cellulose from breadfruit stems is in the range of 70-80% purity. The cellulose-layer can reduce the size of Fe3O4 nanoparticles in preventing agglomeration and become a matrix for Fe3O4 nanoparticles in forming nanocomposites so as to increase adsorption capacity in reducing levels of chromium metal (Cr) in wastewater.

Beri Komentar ?#(0) | Bookmark

Properti	Nilai Properti
ID Publisher	JBPTPPOLBAN
Organisasi
Nama Kontak	Erlin Arvelina
Alamat	Jl. Trsn. Gegerkalong Hilir Ds. Ciwaruga
Kota	Bandung
Daerah	Jawa Barat
Negara	Indonesia
Telepon	022 201 3789 ext. 168, 169, 239
Fax	022 201 3889
E-mail Administrator	erlin.arvelina@polban.ac.id
E-mail CKO	erlin.arvelina@polban.ac.id