The Effect of Steel Fiber on Normal Concrete

Journal from JBPTPPOLBAN / 2022-02-17 07:59:30
Oleh : A. Zulpanani - 196011191988031002 (zulpanani@gmail.com)
Dibuat : 2019-06-07, dengan 1 file

Keyword : Serat Baja Beton Normal
Subjek : Normal Steel Fiber Concrete

Beton adalah suatu campuran yang terdiri dari bahan semen, agregat (halus dan kasar) dan air serta admixture (bila diperlukan). Menurut SNI 03-6468-2000 berdasarkan kuat tekanya beton terbagi dua jenis : Beton Normal dengan f'c < 41.4 Mpa dan Beton Mutu Tinggi dengan f'c ≥ 41.4 Mpa. Menurut ACI 544.3R-84, Serat Baja (Steel Fiber) didefinisikan sebagai serat baja yang mempunyai bentuk kecil-kecil yang rata atau bergelombang, yang didapat dari hasil leburan ekstrak serat-serat baja, yang dalam pemakaianya tersebar merata dalam campuran beton segar dengan aspek rasio yaitu panjang serat dibagi dengan diameter serat (l/d) antara 12.7 mm–63.5 mm. Dalam penelitian ini variasi serat baja dibuat masing-masing 0%, 4% dan 6% terhadap campuran beton yang dibuat, dengan jumlah sampel benda uji 4 buah untuk Kuat Tekan dan 4 buah untuk Split Test (tarik tak langsung) pada umur 14 hari dan 28 hari. Dari hasil pengujian menunjukan bahwa pemakaian serat baja dengan kadar 6% untuk Beton Normal dapat meningkatkan Kuat Tekan dan Kuat Tarik dari beton yang bersangkutan, Hal ini dapat dilihat dari hasil pengujian, dimana pada kadar 0% Kuat Tekan dan Tarik rata-rata pada umur 28 hari = 25.91 Mpa dan 2.80 Mpa. Pada kadar 4% = 30.64 Mpa dan 3.380 Mpa. Pada kadar 6% = 36.99 Mpa dan 3.96 Mpa. Kata Kunci: Serat Baja Beton Normal.

Deskripsi Alternatif :

Concrete is a mixture consisting of cement, aggregate (fine and coarse) and water and admixture (if needed). According to SNI 03-6468-2000 based on the compressive strength of the divided concrete two types: Normal Concrete with f'c < 41.4 Mpa and High Strength Concrete with f'c 41.4 Mpa. According to ACI 544.3R-84, Steel Fiber (Steel Fiber) is defined as a steel fiber having small flat or wavy shapes, which are obtained from the fused extract of steel fibers, which in its use is evenly distributed in the fresh concrete mixture with an aspect ratio of length fiber divided by fiber diameter (l/d) between 12.7 mm–63.5 mm. In this study, variations in steel fibers were made respectively 0%, 4% and 6% of the mixture concrete made, with a total sample of 4 specimens for Compressive Strength and 4 pieces for Split Test (indirect pull) at the age of 14 days and 28 days. From the test results show that the use of steel fiber with a content of 6% for Concrete Normal can increase the compressive strength and tensile strength of the concrete in question seen from the test results, where at the level of 0% Compressive and Tensile Strength on average at the age of 28 days = 25.91 Mpa and 2.80 Mpa. At levels of 4% = 30.64 Mpa and 3.380 Mpa. At 6% = 36.99 Mpa and 3.96 MPa. Keywords: Normal Steel Fiber Concrete.

Beri Komentar ?#(1) | Bookmark

Properti	Nilai Properti
ID Publisher	JBPTPPOLBAN
Organisasi
Nama Kontak	Erlin Arvelina
Alamat	Jl. Trsn. Gegerkalong Hilir Ds. Ciwaruga
Kota	Bandung
Daerah	Jawa Barat
Negara	Indonesia
Telepon	022 201 3789 ext. 168, 169, 239
Fax	022 201 3889
E-mail Administrator	erlin.arvelina@polban.ac.id
E-mail CKO	erlin.arvelina@polban.ac.id