The Effect of pH and Temperature Precipitations on Making Mg/Al Hydrotalcite Catalyst for Glucose Isomerization

Tugas Akhir, 022 / 2021 / TKI
Undergraduate Theses from JBPTPPOLBAN / 2024-01-18 09:52:14
Oleh : C. Yudha Hidayatulloh - 181411039 & Solehuddin Al-Ayubi - 181411061 (c.yudha.tki18@polban.ac.id)
Dibuat : 2024-01-18, dengan 4 file

Keyword : Effect, pH, Temperature, Precipitations, Mg/Al Hydrotalcite, Catalyst, Glucose Isomerization
Subjek : Pengaruh, pH, Suhu Presipitasi, Katalis Hidrotalsit Mg/Al, Isomerisasi Glukosa

Hidrotalsit Mg/Al dibuat dengan bahan utama Mg(NO3)2.6H2O dan Al(NO3)3.9H2O secara kopresipitasi sesuai analisis variasi pH dan suhu presipitasi menggunakan metode Response Surface Method (RSM). Sampel Hidrotalsit Mg/Al yang telah diaktivasi secara kalsinasi selama 3 jam pada suhu 500°C kemudian dianalisis menggunakan Fourier Transform Infrared (FTIR) untuk mengetahui gugus fungsi, Brunauer-Emmett-Teller (BET) untuk mengetahui luas permukaan dan ukuran partikel yang terbentuk, serta X-Ray Diffraction (XRD) untuk mengetahui difraktogram kristal dengan memerhatikan standar Joint Committee on Powder Diffraction Standards (JCPDS) No. 14-0191. Massa terbesar Hidrotalsit Mg/Al dicapai pada kondisi operasi pH 9 dengan suhu presipitasi 45°C, yaitu 4,52 gram, sehingga yield perolehan massa sebesar 73,03%. Hidrotalsit Mg/Al diuji performanya untuk isomerisasi Glukosa menjadi Fruktosa, menghasilkan yield terbesar 20,14% dan selektivitas terbesar 62,40%, yang dicapai oleh Hidrotalsit Mg/Al pada kondisi operasi pH 9 dengan suhu presipitasi 45°C. Kemudian, nilai konversi terbesar 53,47% dicapai oleh katalis kondisi operasi pH 11,12 dengan suhu presipitasi 45°C. Hasil analisis menggunakan RSM menunjukkan bahwa Hidrotalsit Mg/Al yang dibuat dengan variasi pH dan suhu presipitasi tidak memberikan pengaruh yang signifikan baik terhadap perolehan massa Hidrotalsit Mg/Al ataupun proses isomerisasi, termasuk yield, selektivitas, dan konversi, karena nilai P-value menunjukkan angka lebih dari 0,05.

Deskripsi Alternatif :

Hydrotalcite Mg/Al was made with the main components Mg(NO3)2.6H2O and Al(NO3)3.9H2O by coprecipitation according to the analysis of variations in pH and temperature of precipitation using Response Surface Method (RSM). Hydrotalcite Mg/Al samples, which had been activated by calcination for 3 hours at a temperature of 500°C, were then analyzed using Fourier Transform Infrared (FTIR) to determine the functional group, Brunauer-Emmett-Teller (BET) to determine the surface area and particle size formed, and X-Ray Diffraction (XRD) to determine the crystal diffractogram with Joint Committee on Powder Diffraction Standard (JCPDS) No. 14-0191. The mass of Hydrotalcite Mg/Al reached the largest at operating conditions of pH 9 with a precipitation temperature of 45°C, which was 4.52 grams, so that the yield was 73.03%. Hydrotalcite Mg/Al was tested for its performance in the isomerization of Glucose to Fructose, with the largest yield of 20.14% and the highest selectivity of 62.40%, achieved by Hydrotalcite Mg/Al at operating conditions pH 9 with a precipitation temperature of 45°C. Then the highest conversion of 53.47% was achieved by the catalyst operating under conditions of pH 11.12 with a precipitation temperature of 45°C. The results of the RSM analysis showed that Hydrotalcite Mg/Al made with variations in pH and temperature of precipitation did not have a significant effect on either the mass gain of Hydrotalcite Mg/Al or the isomerization process, including selectivity and conversion, because the P-value showed more than 0.05.

Beri Komentar ?#(0) | Bookmark

Properti	Nilai Properti
ID Publisher	JBPTPPOLBAN
Organisasi
Nama Kontak	Erlin Arvelina
Alamat	Jl. Trsn. Gegerkalong Hilir Ds. Ciwaruga
Kota	Bandung
Daerah	Jawa Barat
Negara	Indonesia
Telepon	022 201 3789 ext. 168, 169, 239
Fax	022 201 3889
E-mail Administrator	erlin.arvelina@polban.ac.id
E-mail CKO	erlin.arvelina@polban.ac.id