The Making Of Peanut Shell Briquette With Adhesive Materials Concentration Variation

Tugas Akhir, 007 / 2013 / TEN
Undergraduate Theses from JBPTPPOLBAN / 2017-04-18 15:49:42
Oleh : Diyar Fadila - 101711043 (fadiladiyar@gmail.com)
Dibuat : 2017-04-18, dengan 4 file

Keyword : Briket, Kulit Kacang Tanah, Konsentrasi Bahan Perekat, Efisiensi
Subjek : Briquette, Peanut Shell, Concentration of Adhesives Material, Efficiency

Briket biomassa merupakan bahan bakar yang berasal dari bahan nabati, seperti limbah, perkebunan, pertanian, limbah organik rumah tangga dan lain-lain. Salah satu limbah pertanian yang masih belum termanfaatkan secara maksimal yaitu kulit kacang tanah. Selain sifatnya sebagai limbah, kulit kacang tanah memiliki nilai kalor yang tinggi yaitu 4.850 cal/g. Pembuatan tugas akhir ini bertujuan untuk mengetahui karakteristik briket kulit kacang tanah dengan variasi konsentrasi bahan perekat, sehingga dapat ditemukan konsentrasi bahan perekat yang optimal. Pengujian dilakukan dengan membuat briket kulit kacang tanah dengan tiga variasi konsentrasi bahan perekat (8%, 10% dan 12%). Berdasarkan pengujian yang telah dilakukan, menunjukan bahwa konsentrasi bahan perekat tapioka berpengaruh terhadap karakteristik briket yang dihasilkan. Konsentrasi bahan perekat yang optimal didapat pada konsentrasi 12%, dengan nilai kadar air terendah (9,11%), kadar abu terendah (10,41%), volatille matter tertinggi (63,02%), fixed carbon tertinggi (17,46%), total carbon tertinggi (43,97%), nilai kalor tertinggi (3.952 cal/g), kuat tekan tertinggi (80,172 kg/cm2) dan kerapatan massa tertinggi (1,784 g/cm3). Selain itu dari pengujian briket kulit kacang tanah dengan menggunakan tungku pembakaran, didapat nilai efisiensi tertinggi (20,33%), titik didih air tertinggi (96,8⁰C) dan waktu pencapaian titik didih selama (15 menit). Kata Kunci: Briket, Kulit Kacang Tanah, Konsentrasi Bahan Perekat, Efisiensi.

Deskripsi Alternatif :

Biomass briquette is a fuel derived from plant materials, such as waste plantations, agriculture, household organic waste and others. Much of agricultural waste are still not exploited to the fullest the peanut shell that has a high calorific value is 4,850 cal/g. The objective this final project is to investigate the characteristics of peanut shell briquettes with various concentrations of adhesive material. In this research, there where using three variations of adhesive material concentration (8%, 10% and 12%). The results showed that the concentration of starch adhesives effect on the characteristics of the resulting briquettes. Optimal concentration adhesives obtained at a concentration of 12%, with thar the lowest water content (9.11%), the lowest ash content (10.41%), the highest volatille matter (63.02%), the highest fixed carbon (17.46%), the highest total carbon (43.97%), the highest calorific value (3,952 cal/g), the highest compressive strength (80.172 kg/cm2), and the highest mass density (1.784 g/cm3). In addition, the results of testing peanut shell briquettes using a furnace obtained the highest efficiency value (20.33%), the highest boiling point of water (96.8⁰C) and 15 minutes of a boiling time. Keywords: Briquette, Peanut Shell, Concentration of Adhesives Material, Efficiency.

Beri Komentar ?#(0) | Bookmark

Properti	Nilai Properti
ID Publisher	JBPTPPOLBAN
Organisasi
Nama Kontak	Erlin Arvelina
Alamat	Jl. Trsn. Gegerkalong Hilir Ds. Ciwaruga
Kota	Bandung
Daerah	Jawa Barat
Negara	Indonesia
Telepon	022 201 3789 ext. 168, 169, 239
Fax	022 201 3889
E-mail Administrator	erlin.arvelina@polban.ac.id
E-mail CKO	erlin.arvelina@polban.ac.id