Making of Polyvinyl alcohol (PVA) Composite Nanofiber Using Electrospinning Techniques and The Characterization

Tugas Akhir, 009 / 2019 / ANK
Undergraduate Theses from JBPTPPOLBAN / 2020-03-13 14:36:28
Oleh : Eva Puspita - 161431012 (eva.puspita0505@gmail.com)
Dibuat : 2020-03-13, dengan 4 file

Keyword : Electrospinning, Fe2O3, Kitin, Microwave, nanofiber komposit, PVA, Ultrasonikasi
Subjek : Electrospinning, Fe2O3, Chitin, Microwave, composite nanofiber, PVA, Ultrasonication

Telah dilakukan penelitian mengenai pembuatan nanofiber komposit menggunakan teknik electrospinning. Polimer yang digunakan adalah Polivinil Alkohol (PVA) yang dikompositkan dengan kitin nanofiber, Carbon Black (CB), CuO dan Fe2O3. Kitin yang digunakan merupakan hasil ekstraksi dari cangkang rajungan dan diubah menjadi kitin nanofiber menggunakan metode ultrasonikasi. Fe2O3 yang digunakan merupakan hasil sintesis dengan menggunakan metode Microwave dari prekursor Fe(NO3)3. Karakterisasi nanofiber komposit PVA-Carbon Black-Fe2O3-CuO-Kitin diamati menggunakan SEM-EDS, FTIR, TGA,sudut kontak dan uji antibakteri. Hasil analisis SEM menunjukkan nanofiber komposit yang dibuat mempunyai bentuk seragam dan permukaan yang halus serta mempunyai diameter rata-rata 150-300 nm, sedangkan hasil EDS menunjukkan adanya unsur C, O, Fe dan Cu. Analisis FTIR menunjukkan adanya pita serapan khas komponen penyusun yang ditambahkan dalam nanofiber komposit. Penambahan komposit pada nanofiber PVA menunjukkan adanya peningkatan kestabilan termal dan sudut kontak dengan air yang lebih baik serta hasil uji antibakteri dari nanofiber komposit PVA-Carbon Black-Fe2O3-CuO-Kitin memberikan hasil yang positif dapat menghambat pertumbuhan bakteri Staphylococcus aureus yang ditandai dengan terbentuknya clean zone didaerah sekitar sampel. Kata Kunci: Electrospinning, Fe2O3, Kitin, Microwave, nanofiber komposit, PVA, Ultrasonikasi.

Deskripsi Alternatif :

Research has been conducted on the manufacture of composite nanofiber using electrospinning techniques. The polymers used were Polyvinyl Alcohol (PVA) which were compiled with nanofiber chitin, Carbon Black (CB), CuO and Fe2O3. Chitin used is the result of extraction from crab shells and converted to nanofiber chitin using ultrasonication methods. Fe2O3 used is the result of synthesis using the Microwave method of the Fe(NO3)3 precursor. The characterization of PVA-Carbon Black- Fe2O3-CuO-Chitin nanofiber composites was observed using SEM-EDS, FTIR, TGA, contact angle and antibacterial test. SEM analysis results show that nanofiber composites are made to have uniform shapes and smooth surfaces and have an average diameter of 150-300 nm, while the EDS results indicate the presence of elements C, O, Fe and Cu. FTIR analysis shows the presence of a typical absorption band of the constituent components added in nanofiber composites. The addition of composites to the PVA nanofiber showed an improved thermal stability and contact angle with water as well as the antibacterial test results of the nanofiber composite PVA-Carbon Black- Fe2O3-CuO-Chitin gave positive results that could inhibit the growth of Staphylococcus aureus bacteria characterized by the formation of clean zone in the region around sample. Keywords: Electrospinning, Fe2O3, Chitin, Microwave, composite nanofiber, PVA, Ultrasonication.

Beri Komentar ?#(0) | Bookmark

Properti	Nilai Properti
ID Publisher	JBPTPPOLBAN
Organisasi
Nama Kontak	Erlin Arvelina
Alamat	Jl. Trsn. Gegerkalong Hilir Ds. Ciwaruga
Kota	Bandung
Daerah	Jawa Barat
Negara	Indonesia
Telepon	022 201 3789 ext. 168, 169, 239
Fax	022 201 3889
E-mail Administrator	erlin.arvelina@polban.ac.id
E-mail CKO	erlin.arvelina@polban.ac.id