Utilization of HDPE Plastic Waste and Fly Ash as Filler in Making Paving Block

Tugas Akhir, 034 / 2021 / TKI
Undergraduate Theses from JBPTPPOLBAN / 2024-01-19 09:53:16
Oleh : Fristantia Afininnisa - 181411077 & Rahmi Almalikus Sa'Adah - 181411086 ( fristantia.afininnisa.tki18@polban.ac.id & rahmi.almalikus.tki18@polban.ac.id )
Dibuat : 2024-01-19, dengan 4 file

Keyword : Paving block, HDPE, fly ash.
Subjek : Paving block, HDPE, fly ash.

Limbah HDPE dan fly ash sangat melimpah. Namun demikian pemanfaatan kedua jenis limbah tersebut belum banyak dilakukan. Oleh karena itu salah satu usaha memanfaatkan kedua jenis limbah tersebut adalah dengan memanfaatkannya sebagai bahan substitusi dalam pembuatan bata beton atau paving block. Metoda pemanasan kering dan tanpa pemanasan dapat dilakukan untuk pembuatan benda uji paving block tersebut. Terdapat 9 benda uji modifikasi dan 1 benda uji standard. Sedangkan pengujian kuat tekan, daya serap air dan TDS dilakukan untuk menguji kualitas dari benda uji paving block yang dibuat. Berdasarkan hasil penelitian metoda tanpa pemanasan merupakan metoda terbaik. Sedangkan berdasarkan hasil pengujian kuat tekan yang dilakukan diperoleh benda uji B dan C memberikan nilai kuat tekan yang paling besar yaitu bertutut-turut sebesar 36,733 MPa dan 35,459 MPa. Komposisi berat terbaik benda uji paving block B dan C masing-masing antara semen, kerikil dan pasir, HDPE dan fly ash adalah 1,0%: 4,9% : 0,05%: 0,05% dan 1,0%: 4,8% : 0,1%: 0,1%. Namun demikian jika ditinjau dari pemanfaatan limbah HDPE dan Fly ash, maka direkomendasi benda uji F dan G dengan nilai kuat tekan masing-masing 19,360 MPa dan 17,424 MPa lebih besar dari benda uji standar dengan komposisi antara semen, kerikil dan pasir, HDPE dan fly ash untuk benda uji F adalah 1,0%: 4,5%: 0,2%: 0,3%. Sedangkan untuk benda uji G adalah 1,0%: 4,5%: 0,3%: 0,2%. Peningkatan persen substitusi limbah sampai dengan 12% mengakibatkan terjadi peningkatan kuat tekan yang signifikan berkisar 116,5% sampai dengan 124,3%. Disisi lain, peningkatan persen substitusi limbah sampai dengan 12% memberikan kenaikan dan penurunan daya serap air yang tidak beraturan dalam kisaran 2,32% sampai dengan 3,33%. Sedangkan pengaruh subtitusi fly ash sampai dengan 6% memberikan kenaikan nilai TDS yang tidak signifikan dalam kisaran 0,25% sampai dengan 3,2%.

Deskripsi Alternatif :

HDPE wastes and fly ashes are overflowing. However, the utilization of both these wastes have yet been done. Therefore, one of the ways to utilize these two types of wastes is to use it as a substitute for producing paving block. Dry heating and non-dry heating method can be applied to create the paving block sample. There were 9 modified sample and 1 standard sample. Meanwhile, the examination on compression strength, water absorption, and TDS was done to analyze the quality of the paving block sample. Based on the research result, the non-dry heating method was the best result. Meanwhile, according to the result of the compressive strength test, sample B and C produced the biggest compressive strength values, which was 36,733 MPa and 35,459 MPa, consecutively. The best weight for paving block sample B and C, respectively, between cement, gravel+sand, HDP and fly ash were 1,0%: 4,9%: 0,05%: 0,05% and 1,0%: 4,8%: 0,1%: 0,1%. However, when examined from the utilization of HDPE waste and fly ash, sample F and G was recommended with the compressive strength value, respectively, 19,360 MPa and 17, 424 MPa bigger than the standard sample with composition between cement, gravel+sand, HDPE and fly ash. Sample F valued 1,0%: 4,5%: 0,2%: 0,3%. While sample G valued 1,0%: 4,5%: 0,3%: 0,2%. The increase of waste substitute percentage by 12% resulted in a significant compressive strength increase, ranging from 116,5% to 124,3%. On the other hand, the increase of waste substitute percentage up to 12% resulted in an unstable increase and decrease of water absorption ranging from 2,32% to 3,33%. Meanwhile, the effect of fly ash substitute of 6% resulted in an insignificant increase of TDS value ranging from 0,25% to 3,2%.

Beri Komentar ?#(0) | Bookmark

Properti	Nilai Properti
ID Publisher	JBPTPPOLBAN
Organisasi
Nama Kontak	Erlin Arvelina
Alamat	Jl. Trsn. Gegerkalong Hilir Ds. Ciwaruga
Kota	Bandung
Daerah	Jawa Barat
Negara	Indonesia
Telepon	022 201 3789 ext. 168, 169, 239
Fax	022 201 3889
E-mail Administrator	erlin.arvelina@polban.ac.id
E-mail CKO	erlin.arvelina@polban.ac.id