The Effect of Copper in Nickel Removal Process By Electrodeposition Method

Tugas Akhir, 004 / 2012 / ANK
Undergraduate Theses from JBPTPPOLBAN / 2013-11-08 09:13:55
Oleh : Irma Ariyanti - 091431015 & Siska Rohmatika - 091431025
Dibuat : 2013-09-27, dengan 4 file

Keyword : nikel, recovery, elektrodeposisi, logam pengganggu
Subjek : nickel, recovery, electrodeposition, disturber metal

Logam nikel khususnya dalam bentuk ion Ni2+ merupakan salah satu logam berat yang berbahaya baik bagi lingkungan maupun bagi kesehatan manusia. Untuk mengurangi kadar ion Ni2+ dalam limbah cair elektroplating nikel, salah satu caranya dapat dilakukan melalui proses elektrodeposisi. Prinsip metode elektrodeposisi adalah dengan mengalirkan arus searah melalui larutan elektrolit diantara dua buah elektroda, yaitu logam Cu sebagai katoda dan grafit sebagai anoda. Larutan elektrolit yang digunakan merupakan limbah artifisial elektroplating nikel dengan konsentrasi Ni sebesar 2500 ppm dan larutan elektrolit support (KNO3) dengan konsentrasi 0,1 M. Keberadaan logam lain pada limbah dapat mengganggu proses penyisihan Ni. Oleh karena itu, pada penelitian ini dipelajari pengaruh variabel proses dari tegangan dan konsentrasi logam pengganggu. Tegangan yang digunakan yaitu 1 ; 1,5 dan 2 volt. Sedangkan logam pengganggu yang ditambahkan adalah logam tembaga dengan variasi konsentrasi yaitu 1% ; 5% dan 10%. Dari hasil penelitian proses elektrodeposisi dengan variabel tegangan dan konsentrasi logam pengganggu diperoleh persen penyisihan nikel terbesar terdapat pada tegangan 2 volt dengan persen penyisihan nikel sebanyak 4,01 %. Selain itu, diperoleh persen penyisihan nikel pada konsentrasi 10 % Cu terhadap massa nikel dengan persen penyisihan terbesar sebanyak 10,10 % dengan tegangan sebesar 2 volt. Konstanta laju reaksi pada tegangan 2 volt dengan proses elektrodeposisi menghasilkan nilai konstanta sebesar 2,96 x 102/menit. Sedangkan untuk proses elektrodeposisi yang ditambahkan logam Cu diperoleh konstanta laju reaksi sebesar 4,3 x 10-2/menit. Nilai konstanta yang diperoleh menunjukkan reaksi orde-1. Kata kunci : nikel, recovery, elektrodeposisi, logam pengganggu

Deskripsi Alternatif :

Nickel metal, especially in ionic Ni2+ form is one of heavy metals which is dangerous not only for environment but also for human health. To reduce ion Ni2+ concentration in nickel electroplating wastewater, one way could be done through the electrodeposition process. The principle of electrodeposition method was applying direct current electricity through electrolyte solution between two electrodes, they are Cu as cathode and graphite as anode. The electrolyte solution that used was nickel electroplating artificial waste with Ni concentration was 2500 ppm and electrolyte support solution (KNO3) in concentration of 0,1 M. The existence other metals on waste often disturb the reduce Ni process. Therefore, this research was studied of the influence of process variables from voltage and metal disturber concentrations. The voltage which was used were 1 ; 1,5 and 2 volt. While disturber metal which was added was Cupper with concentration variation were 1% ; 5% and 10%. From the results of electrodeposition process research with variable voltage and metal disturber concentration variable was obtained the biggest of nickel removal percentage was 4,01% for the voltage of 2 volt. Furthermore, was obtained nickel removal percentage at concentration of 10% Cu on a mass nickel with the biggest of nickel removal percentage was 10,10% for the voltage of 2 volt. Constant of reaction velocity in electrodeposition process for the voltage of 2 volt is resulted constant value was 2,96 x 10-2/minutes. While for electrodeposition process which was added Cupper metal in concentration of 10% was obtained rate of reaction constant of 4,3 x 10-2/minutes. Constant value that was obtained showed orde-1 reaction. Keywords : nickel, recovery, electrodeposition, disturber metal

Beri Komentar ?#(0) | Bookmark

Properti	Nilai Properti
ID Publisher	JBPTPPOLBAN
Organisasi
Nama Kontak	Erlin Arvelina
Alamat	Jl. Trsn. Gegerkalong Hilir Ds. Ciwaruga
Kota	Bandung
Daerah	Jawa Barat
Negara	Indonesia
Telepon	022 201 3789 ext. 168, 169, 239
Fax	022 201 3889
E-mail Administrator	erlin.arvelina@polban.ac.id
E-mail CKO	erlin.arvelina@polban.ac.id