Performance Of Porous Concrete by Utilizing Waste Shell Skin as A Replacement of Fine Aggregate

Skripsi, 012 / 2021 / TPPG
Undergraduate Theses from JBPTPPOLBAN / 2022-09-23 13:46:38
Oleh : Januar Dwiki Ramdhani - 171144017 (januar.dwiki.tppg17@polban.ac.id)
Dibuat : 2022-09-23, dengan 4 file

Keyword : beton porous, kulit kerang, kuat tekan dan permeabilitas
Subjek : porous concrete, shells, compressive strength and permeability

Perkembangan dalam pembangunan infrastruktur di daerah perkotaan banyak menggunakan material beton. Dalam penggunaan material beton memiliki dampak negatif yaitu, berkurangnya daerah resapan air hujan di daerah tersebut. Untuk menanggulangi masalah tersebut banyak upaya yang telah dilakukan untuk mengatasi masalah tersebut dan salah satunya ¬¬adalah dengan pembuatan beton berpori (porous). Beton porous adalah salah satu jenis beton dengan porositas tinggi yang di desain agar air dapat masuk melalui pori-pori untuk melewatinya, sehingga dapat meredam limpasan air yang ada di permukaan dan dapat meningkatkan muka air tanah. Dalam penelitian ini bahan komposisi beton porous menggunakan limbah sebagai bahan campuran untuk pembuatan beton porous, yaitu kulit kerang sebagai pengganti agregat halus, dikarenakan di Indonesia sangat berlimpah hasil produksi kerang. Penelitian ini dimulai pada hasil uji material agregat kasar dan pecahan kulit kerang di Laboraturium Bahan Jurusan Teknik Sipil Politeknik Negeri Bandung pada perencanaan campuran beton porous 2 variasi 3% dan 6% kulit kerang sebagai pengganti agregat halus terhadap data sekunder penelitian terdahulu yang akan menghasilkan kuat tekan dan permeabilitas serta mengetahui hasil kinerja beton porous limbah kulit kerang sebagai pengganti agregat halus sesuai dengan ketentuan. Didapatkan hasil perkiraan kuat tekan dan permeabilitas bahwa untuk variasi 3% sebesar 27.78 MPa dan 1.45 cm/detik serta untuk variasi kulit kerang 6% sebesar 27.81 Mpa dan 1.43 cm/detik. Diketahui bahwa nilai kuat tekan beton porous yang menggunakan kulit kerang sebagai pengganti agregat halus berbanding terbalik dengan hasil permeabilitasnya.

Deskripsi Alternatif :

Developments in infrastructure development in urban areas use a lot of concrete material. The use of concrete material has a negative impact, namely, the reduced rainwater catchment area in the area. To overcome this problem, many efforts have been made to overcome this problem and one of them is by making porous concrete. Porous concrete is one type of concrete with high porosity which is designed so that water can enter through the pores to pass through, so that it can reduce runoff water on the surface and can increase the groundwater level. In this study, the composition of porous concrete used waste as a mixture for the manufacture of porous concrete, namely shells as a substitute for fine aggregate, because in Indonesia there are very many shellfish production. This research began on the results of the test of coarse aggregate and shell fragments at the Materials Laboratory of the Department of Civil Engineering at the Bandung State Polytechnic on the planning of a mixture of porous concrete 2 variations of 3% and 6% shells as a substitute for fine aggregate against secondary data of previous research which will produce compressive strength. and permeability as well as knowing the performance results of shell waste porous concrete as a substitute for fine aggregate in accordance with the provisions. It was found that the compressive strength and permeability for the 3% variation were 27.78 MPa and 1.45 cm/second and for the 6% skin variation it was 27.81 MPa and 1.43 cm/second. see that the compressive strength of porous concrete using shells as a substitute for aggregate is inversely proportional to the permeability results.

Beri Komentar ?#(0) | Bookmark

Properti	Nilai Properti
ID Publisher	JBPTPPOLBAN
Organisasi
Nama Kontak	Erlin Arvelina
Alamat	Jl. Trsn. Gegerkalong Hilir Ds. Ciwaruga
Kota	Bandung
Daerah	Jawa Barat
Negara	Indonesia
Telepon	022 201 3789 ext. 168, 169, 239
Fax	022 201 3889
E-mail Administrator	erlin.arvelina@polban.ac.id
E-mail CKO	erlin.arvelina@polban.ac.id