Synthesis of Nanocellulose Based on Corncob by Acid Hydrolysis and Homogenization

Tugas Akhir, 035 / 2021 / TKI
Undergraduate Theses from JBPTPPOLBAN / 2024-01-19 09:56:55
Oleh : Jihan Amilia Nuriansyah - 181411080 & Saripah - 181411092 (jihan.amilia.tki18@polban.ac.id)
Dibuat : 2024-01-19, dengan 4 file

Keyword : Tongkol Jagung, Isolasi Selulosa, Hidrolisis Asam, Homogenisasi
Subjek : Corncob, Cellulose Isolation, Acid Hydrolysis, Homogenization.

Tongkol jagung merupakan limbah pertanian dengan kandungan selulosa yang tinggi yaitu ±41%, sehingga memiliki potensi dimanfaatkan sebagai bahan baku untuk pembuatan nanoselulosa. Nanoselulosa diperoleh dengan mereduksi ukuran selulosa. Proses pembuatan nanoselulosa dari tongkol jagung dilakukan dengan mengisolasi selulosa kemudian dilanjutkan dengan perlakuan kimia yaitu hidrolisis asam dan perlakuan mekanik yaitu homogenisasi untuk mereduksi ukuran selulosa. Proses hidrolisis asam dilakukan menggunakan H2SO4 dengan variasi konsentrasi 56%, 58%, dan 60% pada suhu 50oC selama 90 menit. Proses homogenisasi dilakukan menggunakan blender dengan variasi kecepatan putar 4.099 rpm, 5.519 rpm, dan 6.280 rpm pada suhu 25oC selama 10 menit. Pada penelitian dengan metode hidrolisis asam, rendemen terbanyak diperoleh pada variasi konsentrasi H2SO4 58% dengan rendemen sebesar 29,75% dan pada penelitian dengan metode homogenisasi diketahui bahwa kecepatan homogenisasi 6.280 rpm menghasilkan nanoselulosa dengan ukuran terkecil.

Deskripsi Alternatif :

Corncob is an agricultural waste with a high cellulose content of 41%, and thus has the potential to be used as a raw material for the manufacture of nanocellulose. Nanocellulose is produced by reducing its cellulose size. The nanocellulose manufacture process from the corncob is followed by the chemical treatment of acid hydrolysis and the mechanical treatment of homogenization in order to reduce cellulose in size. The acidic hydrolysis process uses strong acid which is H2SO4 with a concentration variety consist of 56%, 58%, and 60% at 50oC for 90 minutes. The process of homogenization is carried out by using a blender with a variety of speed of 4,099 RPM, 5,519 RPM, and 6,280 RPM at 25oC for 10 minutes. The acid hydrolysis result in high yield with 29,75% of nanocellulose produced by concentration of sulfuric acid 58% while homogenization method on 6,280 rpm of speed is result the smallest produce of nanocellulose than two others speed is used.

Beri Komentar ?#(0) | Bookmark

Properti	Nilai Properti
ID Publisher	JBPTPPOLBAN
Organisasi
Nama Kontak	Erlin Arvelina
Alamat	Jl. Trsn. Gegerkalong Hilir Ds. Ciwaruga
Kota	Bandung
Daerah	Jawa Barat
Negara	Indonesia
Telepon	022 201 3789 ext. 168, 169, 239
Fax	022 201 3889
E-mail Administrator	erlin.arvelina@polban.ac.id
E-mail CKO	erlin.arvelina@polban.ac.id