GDL

Analysis The Effect of Temperature and Hetaing Time of Platina Agglomeration on Pt/Al2O3 Platforming Catalyst

Tugas Akhir, 023 / 2012 / ANK
Undergraduate Theses from JBPTPPOLBAN / 2013-11-08 09:47:22
Oleh : Lian Artini - 091431018
Dibuat : 2013-10-01, dengan 4 file

Keyword : aglomerasi, sintering, katalis platforming, dispersi, surface area, Pt/Al2O3
Subjek : agglomeration, sintering, platforming, dispersion, surface area, Pt/Al2O3

Katalis yang digunakan dalam proses platforming di RU VI- Balongan adalah katalis platforming Pt/Al2O3. Pada prosesnya, katalis platforming mengalami pemanasan dalam reaktor atau regenerator pada temperatur sekitar 490 – 520oC. Penggunaan katalis pada temperatur tinggi (over heating) mendorong terjadinya kerusakan katalis yaitu aglomerasi platina sehingga mengakibatkan dispersi (penyebaran) logam platina pada katalis tidak merata. Hal ini akan mengurangi optimasi katalis pada saat reaksi berlangsung. Menanggulangi hal tersebut dilakukan penelitian ini dengan tujuan untuk mencari suhu pemanasan mulai terjadinya aglomerasi platina dan melihat pengaruh waktu pemanasan terhadap karakteristik katalis platforming Pt/ Al2O3. Aglomerasi platina diketahui dari beberapa parameter yaitu dispersi Pt dengan metode UOP 945-91, jenis kristal/ fasa alumina dengan metode UOP 905-91, surface area dengan metode ASTM D-3663-03, kadar Pt dan kadar Cl dengan menggunakan XRF. Hasil analisis menunjukkan katalis platforming Pt/Al2O3 mulai mengalami aglomerasi platina pada suhu pemanasan 800⁰C 4 jam yang mempengaruhi parameter-parameter fisika-kimia katalis menjadi di bawah nilai standar, yaitu nilai dispersi platina pada katalis menjadi < 0,9 mol/mol, terjadinya perubahan fasa alumina dari gamma alumina menjadi alpha alumina, surface area <150 m2/gr dan kadar klor dalam katalis menjadi < 1,00 %-wt. Kata kunci: aglomerasi, sintering, katalis platforming, dispersi, surface area, Pt/Al2O3

Deskripsi Alternatif :

Catalyst which used on the platforming process in RU VI- Balongan is Pt/Al2O3 platforming catalyst. In the paltforming process, the catalyst was heated in the reactor or regenerator at about 490-520⁰C. Therefore f the catalyst experienced at high temperature (over heating), then the catalyst will damage indicated b platina agglomeration as platina dispersion on catalyst are unever distribution. This then reduce the activity of the catalyst during the paltforming process. The research is aimed to outcome the catalyst damaged by observing temperature and time of heating toward characteristic of Pt/Al2O3 platforming catalyst.

Platina agglomeration is known from several parameters. Firstly, Pt agglomeration can be detected by chemisorbtion using UOP 945-91 methode to indicate Pt dispersion. Secondly, the crystal/ alumina phase can be observed by XRD using UOP 905-91. Thirdly the surface area of the catalyst can be analysed by nitrogen adsorption using ASTM D-3663-03 methode. Finally, the element of the catalyst can be analysed by XRF.

The results influenced physic-chemical properties of the catalyst below to standard a shown by reducing the dispersion value less than 0,9 mol/mol, changing the alumina phase from gamma alumina to alpha alumina, reducing surface area less than 150m2/g and Cl content in the catalyst less than 1,00%-wt.

Keywords: agglomeration, sintering, platforming, dispersion, surface area, Pt/Al2O3

Beri Komentar ?#(0) | Bookmark

Properti	Nilai Properti
ID Publisher	JBPTPPOLBAN
Organisasi
Nama Kontak	Erlin Arvelina
Alamat	Jl. Trsn. Gegerkalong Hilir Ds. Ciwaruga
Kota	Bandung
Daerah	Jawa Barat
Negara	Indonesia
Telepon	022 201 3789 ext. 168, 169, 239
Fax	022 201 3889
E-mail Administrator	erlin.arvelina@polban.ac.id
E-mail CKO	erlin.arvelina@polban.ac.id