Synthesis of Zinc Sulphate and Manganese Sulphate From Waste Zinc Carbon Battery with Crystallization Method

Tugas Akhir, 014 / 2021 / TKI
Undergraduate Theses from JBPTPPOLBAN / 2024-01-16 09:12:21
Oleh : Muhamad Naufal Iftikar Fadhilah - 181411019 & Sismadinia - 181411029 (sismadinia14@gmail.com )
Dibuat : 2024-01-16, dengan 4 file

Keyword : Battery waste, Carbon zinc battery waste, zinc sulfate, manganese sulfate, crystallization.
Subjek : Limbah baterai, Limbah baterai seng karbon, seng sulfat, mangan sulfat, kristalisasi.

Baterai primer seng karbon merupakan baterai yang sering digunakan sehingga menghasilkan limbah yang cukup melimpah. Limbah baterai mengandung logam berat seperti seng dan mangan yang dapat mencemarkan lingkungan serta dapat menyebabkan dampak buruk bagi kesehatan. Penelitian ini dilakukan untuk memanfaatkan limbah baterai seng karbon menjadi ZnSO4 dari anoda yang berupa seng dan MnSO4 dari pastanya dengan metode kristalisasi. Tujuannya adalah menentukan konsentrasi asam sulfat untuk menentukan yield maksimum pada sintesis ZnSO4, konsentrasi asam oksalat untuk menentukan yield maksimum pada sintesis MnSO4 serta menentukan jumlah molekul air yang terikat pada produk dengan analisis gravimetri. Sintesis seng sulfat dilakukan dengan melarutkan 5 gram logam seng dalam 80 mL asam sulfat. Variasi konsentrasi 5%, 10%, 15%, 20%, 25% dan 30% pada suhu 80oC dan kecepatan pengadukan 300 rpm. Sintesis mangan sulfat dilakukan dengan melarutkan 5 gram pasta dalam 10 mL asam sulfat 25% dan 80 mL asam oksalat sebagai pereduksi. Variasi konsentrasi 2%, 4%, 6%, 8%, 10% pada suhu 80oC dan kecepatan pengadukan 300 rpm. Hasil seng sulfat maksimum diperoleh 12,20 gram dan yieldnya 81,50% pada 80 mL konsentrasi asam sulfat 25%. Hasil mangan sulfat maksimum yaitu 4,22 gram dan yield yaitu 53,24% pada konsentrasi asam oksalat 4%. Jumlah molekul air yang terikat pada seng sulfat yaitu 2 sehingga rumus senyawa adalah ZnSO4.2H2O dan mangan sulfat yaitu 1 sehingga menjadi senyawa MnSO4.H2O.

Deskripsi Alternatif :

A zinc-carbon primary battery was a battery that was often used so that it produced quite a lot of waste. Battery waste contained heavy metals such as zinc and manganese which could pollute the environment and could cause adverse health effects. This research was conducted to utilize zinc-carbon battery waste into ZnSO4 from the anode in the form of zinc and MnSO4 from its paste by crystallization method. The aim was to determine the concentration of sulfuric acid to determine the maximum yield in the synthesis of ZnSO4, the concentration of oxalic acid to determine the maximum yield of the synthesis of MnSO4, and to determine the number of water molecules bound to the product by gravimetric analysis. Synthesis of zinc sulfate was carried out by dissolving 5 grams of metallic zinc in 80 mL of sulfuric acid. Concentration variations of 5%, 10%, 15%, 20%, 25% and 30% at a temperature of 80oC and a stirring speed of 300 rpm. The synthesis of manganese sulfate was carried out by dissolving 5 grams of paste in 10 mL of 25% sulfuric acid and 80 mL of oxalic acid as a reducing agent. Concentration variations of 2%, 4%, 6%, 8%, 10% at a temperature of 80oC and a stirring speed of 300 rpm. The maximum yield of zinc sulfate was 12.20 grams and the yield was 81.50% at 80 mL of 25% sulfuric acid concentration. The maximum yield of manganese sulfate was 4.22 grams and the yield is 53.24% at a concentration of 4% oxalic acid. The number of water molecules bound to zinc sulfate was 2 so that the formula for the compound is ZnSO4.2H2O and manganese sulfate was 1 so that it became a compound MnSO4.H2O.

Beri Komentar ?#(0) | Bookmark

Properti	Nilai Properti
ID Publisher	JBPTPPOLBAN
Organisasi
Nama Kontak	Erlin Arvelina
Alamat	Jl. Trsn. Gegerkalong Hilir Ds. Ciwaruga
Kota	Bandung
Daerah	Jawa Barat
Negara	Indonesia
Telepon	022 201 3789 ext. 168, 169, 239
Fax	022 201 3889
E-mail Administrator	erlin.arvelina@polban.ac.id
E-mail CKO	erlin.arvelina@polban.ac.id