Design and Manufacturing of Triblogy Testing Machine Type Pin-on-disc (Part Arm and Jig)

Tugas Akhir, 031 / 2013 / TME
Undergraduate Theses from JBPTPPOLBAN / 2017-03-23 09:58:55
Oleh : Muhammad Zain - 101211058 & Basthomy Zulfy - 101211070 (muhammadzein19@gmail.com; BasthomyZ@gmail.com)
Dibuat : 2017-03-23, dengan 4 file

Keyword : Pin on disk, keausan, alat uji, ASTM G99
Subjek : Pin on disc, wear and tear, test equipment, ASTM G99

Pada suatu sistem permesinan, kontak antar permukaan komponen menjadi sebuah fenomena yang wajar terjadi. Kontak antar komponen yang dikenakan sebuah gaya mekanik maka akan timbul suatu fenomena yang disebut sebagai keausan (wear). Oleh karena itu penentuan tingkat keausan suatu material sangat dibutuhkan untuk menentukan tingkat efisiensi mesin, waktu pakai, desain mesin dan pemeliharaan mesin. Dalam tugas akhir ini dibuat sebuah alat uji keausan dengan metode pin on disk bagian lengan uji dan pencekam spesimen. Dalam proses perancangan alat uji tersebut dibutuhkan data referensi berupa standar alat uji yaitu ASTM G99 dan data acuan berupa desain alat uji yang telah ada. Pada proses pembuatan dibutuhkan banyak aspek yang ditentukan oleh standar ASTM G99 seperti kekerasan pin uji, sistem pembebanan dan kecepatan putar spesimen. Lalu proses pengujian dilakukan pada 2 parameter yang divariasikan, yaitu parameter Material spesimen: Low Carbon Steel St37 dan Duralumunium dan jarak luncur keausan (Distance) Dari hasil Pengujian didapatkan data berupa volumeloss pada spesimen, yaitu berupa volume loss diketahui bahwa spesimen 1 yaitu Low Carbon Steel St37 memiliki nilai volume loss lebih rendah dari spesimen 2 duralumunium, serta diketahui pula pengaruh jarak gesekan terhadap keausan yaitu nilai volume loss yang semakin kecil pada jarak yang semakin jauh dari pusat. Kata kunci: Pin on disk, keausan, alat uji, ASTM G99.

Deskripsi Alternatif :

At a machining system, contact between the surface of the component to be a phenomenon that occurs naturally. Contact between components are subject to a mechanical force will give rise to a phenomenon known as wear and tear (wear). Therefore the determination of the wear rate of a material is needed to determine the level of engine efficiency, time wear, engine design and engine maintenance. In this thesis made a wear test equipment with pin on disk method sleeves and chucks test specimen. In the process of designing the test equipment required in the form of standard reference data that is ASTM G99 test equipment and reference data in the form of design of existing test equipment. In the process it takes a lot of aspects are determined by standards such as ASTM G99 pin hardness test, the loading system and specimen rotation speed. Then the process of testing performed on 2 parameters are varied, the parameters of the specimens Material: Low Carbon Steel St37 and Duralumunium and wear of sliding distance (Distance) Testing results obtained from the data in the form of volumeloss on the specimen, in the form of volume loss is known that specimen 1 Low Carbon Steel St37 volume loss has a value lower than 2 duralumunium specimens, and is also known to influence the wear of the friction distance value is the smaller the volume loss in the farther the distance from the center. Keywords: Pin on disc, wear and tear, test equipment, ASTM G99.

Beri Komentar ?#(0) | Bookmark

Properti	Nilai Properti
ID Publisher	JBPTPPOLBAN
Organisasi
Nama Kontak	Erlin Arvelina
Alamat	Jl. Trsn. Gegerkalong Hilir Ds. Ciwaruga
Kota	Bandung
Daerah	Jawa Barat
Negara	Indonesia
Telepon	022 201 3789 ext. 168, 169, 239
Fax	022 201 3889
E-mail Administrator	erlin.arvelina@polban.ac.id
E-mail CKO	erlin.arvelina@polban.ac.id