Effect of Current Variation GTAW Process to Physic and Mechanical Properties Austenitic Stainless Steel AISI 316L

Tugas Akhir, 025 / 2017 / TME
Undergraduate Theses from JBPTPPOLBAN / 2018-01-12 08:18:04
Oleh : Sinatrya Azali Aryadhani - 141211029 (sinatrya@ymail.com)
Dibuat : 2018-01-12, dengan 4 file

Keyword : Baja tahan karat austenitik AISI 316L, Gas Tungsten Arc Welding, daerah terpengaruh panas, Arus, Uji tarik, Uji Keras, Makrostruktur, Mikrostruktur
Subjek : Austenitic stainless steel AISI 316L, Gas Tungsten Arc Welding, heat affected zone ,Current, Tensile Test, Hardness test, Macrostructure, Microstructure

Penelitian ini bertujuan untuk mengetahui pengaruh variasi arus proses GTAW terhadap sifat fisik dan mekanik pada baja tahan karat austenitik AISI 316L. Material baja tahan karat austenitik 316L memiliki sifat ketahanan korosi dan sifat mekanis yang baik[6]. Penentuan parameter pengelasan dapat mempengaruhi sifat fisik dan mekanik dari pengelasan yang dilakukan terutama pada HAZ dengan variasi arus 60A, 70A, 80A dengan bahan tambah ER316L. Ketika proses pengelasan dilakukan, karbon tipe 316L yang lebih rendah memungkinkan pengurangan ketahanan korosi intergranular yang disebabkan oleh kromium karbida yang terbentuk dari proses pengelasan[1]. Pengujian tarik dan kekerasan dilakukan untuk mendapatkan sifat mekanik, serta pemeriksaan makrostruktur dan mikrostruktur untuk pembuktian sifat fisiknya. Pembuatan spesimen uji berdasarkan hasil pemeriksaan radiography sinar X dari hasil pengelasan baja tahan karat austenitik AISI 316L. Hasil pemeriksaan makrostruktur bahwa arus terbesar memiliki HAZ yang lebih panjang, sedangkan pemeriksaan mikrostuktur menghasilkan struktur dengan fasa dominan austenitik. Arus yang terendah menghasilkan kekerasan yang tinggi pada HAZ, sementara arus tertinggi menghasilkan kekerasan yang rendah pada HAZ. Arus 80A memiliki kekuatan tarik tertinggi dan kekuatan luluh yang tertinggi dibandingkan arus 60A dan 70A dimana 60A terendah. Arus 80A merupakan arus terbaik pada pengelasan GTAW baja tahan karat austenitik AISI 316L dilihat dari sifat mekanik yang dihasilkan. Pada saat proses pengelasan sebaiknya menggunakan jig yang lebih memadai untuk mengurangi distorsi yang dihasilkan. Kata kunci: Baja tahan karat austenitik AISI 316L, Gas Tungsten Arc Welding, daerah terpengaruh panas, Arus, Uji tarik, Uji Keras, Makrostruktur, Mikrostruktur.

Deskripsi Alternatif :

This study aims to determine the effect of GTAW process current variation on physical and mechanical properties in AISI 316L austenitic stainless steel. The stainless steel austenitic AISI 316L material has excellent corrosion resistance and mechanical properties[6]. Determination of welding parameters can affect the physical and mechanical properties of the welding carried out mainly on HAZ with variations of current 60A, 70A, 80A with ER316L added materials. When welding operations are used, a lower type 316L carbon allows for the reduction of intergranular corrosion resistance caused by chromium carbide formed by the welding process[1]. Tensile and hard tests are performed to obtain mechanical properties, as well as macrostructural and microstructural checks to verify their physical properties. The manufacture of test specimens based on X-ray radiography results from AISI 316L austenitic stainless steel welding. The macrostructure examination results that the largest current has a longer HAZ, while the microstructure examination results in an auntenite bermatriks structure. The lowest current produces high hardness in HAZ, while the highest current produces low hardness in HAZ. Current 80A has the highest tensile strength and yield strength between the currents 60A and 70A where the lower 60A. The 80A current is the best current in the AISI 316L austenitic stainless steel GTAW welding seen from the resulting mechanical properties. At the time of the welding process it is better to use a more adequate jig to reduce the resulting distortion. Keywords: Austenitic stainless steel AISI 316L, Gas Tungsten Arc Welding, heat affected zone ,Current, Tensile Test, Hardness test, Macrostructure, Microstructure.

Beri Komentar ?#(0) | Bookmark

Properti	Nilai Properti
ID Publisher	JBPTPPOLBAN
Organisasi
Nama Kontak	Erlin Arvelina
Alamat	Jl. Trsn. Gegerkalong Hilir Ds. Ciwaruga
Kota	Bandung
Daerah	Jawa Barat
Negara	Indonesia
Telepon	022 201 3789 ext. 168, 169, 239
Fax	022 201 3889
E-mail Administrator	erlin.arvelina@polban.ac.id
E-mail CKO	erlin.arvelina@polban.ac.id