Sintesis dan Karakterisasi ZSM-5 (Zeolite Socony Mobile-5) tanpa Template menggunakan Metode Hidrotermal
Synthesis and Characterization of ZSM-5 (Zeolite Socony Mobile-5) without Template using Hydrothermal Method
Tugas Akhir, 009 / ANK / 2020Undergraduate Theses from JBPTPPOLBAN / 2021-11-02 10:39:31
By : Oktaviani Indah Purnamasari - 171431018 & Shifa Amadea Deviana - 171431025 ( oktaviani.indah.anki17@polban.ac.id )
Created : 2021-11-02, with 4 files
Keyword : ZSM-5, template, hydrothermal method, ratio, characterization.
Subject : ZSM-5, template, metode hidrotermal, rasio, karakterisasi.
ZSM-5 (Zeolite Socony Mobile-5) merupakan katalis zeolite sintetik yang sering digunakan pada berbagai industri kimia. Pada penelitian ini dilakukan sintesis ZSM-5 tanpa template menggunakan metode hidrotermal dengan variasi rasio mol SiO2/Al2O3 sebesar 30, 50 dan 80, perbandingan mol yang digunakan adalah 0,5 SiO2: x Al2O3: 17,5 H2O, x= 0,0167, 0,0100, 0,0062. Bahan baku yang digunakan adalah natrium silika sebagai sumber silika dan aluminium sulfat sebagai sumber alumina. Padatan serbuk ZSM-5 hasil sintesis dikarakterisasi dengan Spektroskopi Fourier Transform Infrared (FTIR), uji luas permukaan dan uji keasaman. Rasio mol terbaik SiO2/Al2O3 pada penelitian sintesis ZSM-5 ini diperoleh pada nilai 80, dengan hasil karakterisasi pada uji FTIR terdapat beberapa puncak yang menunjukkan adanya ciri-ciri spesifik zeolit ZSM-5, seperti adanya vibrasi ulur simetri TO4 (T = atom Si atau Al) pada bilangan gelombang sekiar 600-500 cm-1 dan puncak yang merupakan ciri spesifik struktur zeolite tipe MFI. Bilangan gelombang tersebut menunjukkan vibrasi framework pada struktur molekul cincin segi lima, terlihat pada puncak bilangan gelombang 543.59 cm-1, dengan nilai keasaman sebesar 2,19 mmol/gram dan luas permukaan sebesar 330,9943 m2/gram.
Description Alternative :ZSM-5 (Zeolite Socony Mobile-5) is a synthetic zeolite catalyst that is often used in various chemical industries. In this study, ZSM-5 synthesis without awas carried out template using the hydrothermal method with a variation of the mole ratio SiO2/ Al2O3 of 30, 50 and 80, the mole ratio used was 0,5 SiO2: x Al2O3: 17, 5 H2O, x = 0,0167; 0,0100; 00062. The raw material used is sodium silica as a source of silica and aluminum sulfate as a source of alumina. The synthesized ZSM-5 powder solid was characterized by Spectroscopy Fourier Transform Infrared (FTIR), surface area test and acidity test. The best mole ratio of SiO2/ Al2O3 in the ZSM-5 synthesis study was obtained at a value of 80, with the results of characterization in the FTIR test there were several peaks that indicated the specific characteristics of ZSM-5 zeolite, such as the tensile vibration of TO4 (T = Si or Al atoms) at a wave number around 600-500 cm-1 and a peak which is a specific feature of the MFI-type zeolite structure. The wave numbers shows vibration framework at the molecular structure of a pentagon-shaped rings, seen at the height of 543,59 cm-1 wave numbers, with acidity value of 2,19 mmol/g and a surface area of 330,9943 m2/ gram.
Property | Value |
---|---|
Publisher ID | JBPTPPOLBAN |
Organization | |
Contact Name | Erlin Arvelina |
Address | Jl. Trsn. Gegerkalong Hilir Ds. Ciwaruga |
City | Bandung |
Region | Jawa Barat |
Country | Indonesia |
Phone | 022 201 3789 ext. 168, 169, 239 |
Fax | 022 201 3889 |
Administrator E-mail | erlin.arvelina@polban.ac.id |
CKO E-mail | erlin.arvelina@polban.ac.id |
Print ...
Contributor...
- Pembimbing 1: Dr. Eko Andrijanto, LRSC.
Pembimbing 2: Drs. Apt. Budi Santoso, M.T., Editor: Muhammad Abdillah Islamy, S.Pd
Downnload...
File : KELENGKAPAN TA - 171431018 & 171431025.pdf
(942287 bytes)
File : BAB 1 - 171431018 & 171431025.pdf
(85016 bytes)
File : BAB 2 - 171431018 & 171431025.pdf
(284873 bytes)
File : BAB 5 - 171431018 & 171431025.pdf
(74466 bytes)