Synthesis and Characterization of ZSM-5 (Zeolite Socony Mobile-5) without Template using Hydrothermal Method

Tugas Akhir, 009 / ANK / 2020
Undergraduate Theses from JBPTPPOLBAN / 2021-11-02 10:39:31
Oleh : Oktaviani Indah Purnamasari - 171431018 & Shifa Amadea Deviana - 171431025 ( oktaviani.indah.anki17@polban.ac.id )
Dibuat : 2021-11-02, dengan 4 file

Keyword : ZSM-5, template, hydrothermal method, ratio, characterization.
Subjek : ZSM-5, template, metode hidrotermal, rasio, karakterisasi.

ZSM-5 (Zeolite Socony Mobile-5) merupakan katalis zeolite sintetik yang sering digunakan pada berbagai industri kimia. Pada penelitian ini dilakukan sintesis ZSM-5 tanpa template menggunakan metode hidrotermal dengan variasi rasio mol SiO2/Al2O3 sebesar 30, 50 dan 80, perbandingan mol yang digunakan adalah 0,5 SiO2: x Al2O3: 17,5 H2O, x= 0,0167, 0,0100, 0,0062. Bahan baku yang digunakan adalah natrium silika sebagai sumber silika dan aluminium sulfat sebagai sumber alumina. Padatan serbuk ZSM-5 hasil sintesis dikarakterisasi dengan Spektroskopi Fourier Transform Infrared (FTIR), uji luas permukaan dan uji keasaman. Rasio mol terbaik SiO2/Al2O3 pada penelitian sintesis ZSM-5 ini diperoleh pada nilai 80, dengan hasil karakterisasi pada uji FTIR terdapat beberapa puncak yang menunjukkan adanya ciri-ciri spesifik zeolit ZSM-5, seperti adanya vibrasi ulur simetri TO4 (T = atom Si atau Al) pada bilangan gelombang sekiar 600-500 cm-1 dan puncak yang merupakan ciri spesifik struktur zeolite tipe MFI. Bilangan gelombang tersebut menunjukkan vibrasi framework pada struktur molekul cincin segi lima, terlihat pada puncak bilangan gelombang 543.59 cm-1, dengan nilai keasaman sebesar 2,19 mmol/gram dan luas permukaan sebesar 330,9943 m2/gram.

Deskripsi Alternatif :

ZSM-5 (Zeolite Socony Mobile-5) is a synthetic zeolite catalyst that is often used in various chemical industries. In this study, ZSM-5 synthesis without awas carried out template using the hydrothermal method with a variation of the mole ratio SiO2/ Al2O3 of 30, 50 and 80, the mole ratio used was 0,5 SiO2: x Al2O3: 17, 5 H2O, x = 0,0167; 0,0100; 00062. The raw material used is sodium silica as a source of silica and aluminum sulfate as a source of alumina. The synthesized ZSM-5 powder solid was characterized by Spectroscopy Fourier Transform Infrared (FTIR), surface area test and acidity test. The best mole ratio of SiO2/ Al2O3 in the ZSM-5 synthesis study was obtained at a value of 80, with the results of characterization in the FTIR test there were several peaks that indicated the specific characteristics of ZSM-5 zeolite, such as the tensile vibration of TO4 (T = Si or Al atoms) at a wave number around 600-500 cm-1 and a peak which is a specific feature of the MFI-type zeolite structure. The wave numbers shows vibration framework at the molecular structure of a pentagon-shaped rings, seen at the height of 543,59 cm-1 wave numbers, with acidity value of 2,19 mmol/g and a surface area of 330,9943 m2/ gram.

Beri Komentar ?#(0) | Bookmark

Properti	Nilai Properti
ID Publisher	JBPTPPOLBAN
Organisasi
Nama Kontak	Erlin Arvelina
Alamat	Jl. Trsn. Gegerkalong Hilir Ds. Ciwaruga
Kota	Bandung
Daerah	Jawa Barat
Negara	Indonesia
Telepon	022 201 3789 ext. 168, 169, 239
Fax	022 201 3889
E-mail Administrator	erlin.arvelina@polban.ac.id
E-mail CKO	erlin.arvelina@polban.ac.id