Synthesis and Characterization of Zirconia (HAp-Zr) NanoHydroxycates for Lung Cancer Therapy

Tugas Akhir, 015 / ANK / 2020
Undergraduate Theses from JBPTPPOLBAN / 2021-11-04 10:01:16
By : Whysnu Akbar Okta Pradana - 171331032 ( viviratuandaresta@gmail.com )
Created : 2021-11-04, with 4 files

Keyword : Lung cancer, Hydroxyapatite Nanoparticles, Zirconium, Doping.
Subject : Kanker paru, Hidroksiapatit Nanopartikel, Zirkonium, Doping.

Kanker paru merupakan jenis kanker yang paling sering muncul dan sebagai penyebab kematian tertinggi dengan jumlah kasus sebesar 2,09 juta kasus yang menyebabkan 1,76 juta kematian. Pengembangan teknik photodynamic therapy menggunakan hidroksiapatit nanopartikel (HAp-N) dengan doping logam inert berukuran 200 nm untuk terapi kanker paru telah dilakukan. Pada penelitian ini dilakukan sintesis HAp-N dengan doping logam Zirkonium (Zr) sebagai alternatif untuk memberikan efek Reactive Oxygen Species (ROS) yang dapat menghancurkan sel tumor. Telah dilakukan sintesis nanopartikel hidroksiapatit (HAPNs) melalui reaksi antara kalsium (CaCl2) dan fosfat ((NH4)3HPO4). Logam Zr yang didoping ke dalam HAp sebanyak 10% dari mol HAp yang dipreparasi pada konsentrasi 1000 ug/mL. Intensitas relatif pada difraktogram dapat teramati berkurang pada HAp yang didoping dengan Zr dibandingkan dengan HAp tanpa doping, tanpa menunjukkan terjadinya perubahan struktur kristal. Hasil pengukuran SEM-EDS menunjukkan krital HAp membentuk aglomer spherical dengan diameter 5 – 10 um sementara itu HAp-Zr membentuk aglomer jarum dengan ukuran 10 – 50 um. Perbandingan Ca/P kristal HAp sebesar 1.95 sementara HAp-Zr 1.38. Alternatif penggunaan sitrat dan ultra sonikasi terbukti dapat menekan agregasi sehingga diameter dari HAp setengah kali lebih kecil dibandingkan diameter hidrodinamis HAp tanpa sitrat. Waktu optimum proses ultra sonikasi nanopartikel HAp adalah 240 menit. Proses penambahan sitrat dan ultra sonikasi menghasilkan ukuran dispersi HAp di dalam air sebesar 241,5 nm dan diameter hidrodinamis dari HAp-Zr di dalam air berkisar antara 119 nm sampai 138 nm. Hasil penelitian ini menunjukkan HAp-Zr nanopartikel telah berhasil disintesis dengan ukuran hidrodinamis antara 100 – 200 nm untuk selanjutnya dapat dilakukan uji aktivitas antikanker paru secara invitro dan invivo.

Description Alternative :

Lung cancer is the most common type of cancer and the leading cause of death with 2.09 million cases causing 1.76 million deaths. Development of a photodynamic therapy technique using hydroxyapatite nanoparticles (HAp-N) with 200 nm doped inert metal for lung cancer therapy has been carried out. In this study, the synthesis of HAp-N doped with zirconium (Zr) metal as an alternative to provide the effect of Reactive Oxygen Species (ROS) which can destroy tumor cells. The synthesis of hydroxyapatite nanoparticles (HAPNs) through the reaction between calcium (CaCl2) and phosphate ((NH4)3HPO4) has been carried out. The Zr metal doped into HAp was 10% of the moles of HAp prepared at a concentration of 1000 µg / mL. The relative intensity of the diffractogram was observed to be reduced in HAp doped with Zr compared to HAp without doping, indicating no change in crystal structure. SEM-EDS measurement results show that HAp crystals form spherical agglomerates with a diameter of 5 - 10 um while HAp-Zr forms needle agglomerates with a size of 10 - 50 um. The ratio of Ca/P for HAp crystals is 1.95 while HAp-Zr is 1.38. Alternative of adding citrate and ultra sonication proved to be able to overcome aggregation so that the diameter of the HAp is half smaller than the hydrodynamic diameter of the HAp without adding citrate. The optimum ultra sonication time for HAp nanoparticles is 240 minutes. The process of adding citrate and ultra sonication resulted in a dispersion size of HAp in water is 241.5 nm and a hydrodynamic diameter of HAp-Zr in water ranging from 119 nm to 138 nm. The results of this study indicate that HAp-Zr nanoparticles have been successfully synthesized with hydrodynamic sizes between 100 - 200 nm, so that invitro and invivo lung anticancer activity tests can be carried out.

Give Comment ?#(1) | Bookmark

Property	Value
Publisher ID	JBPTPPOLBAN
Organization
Contact Name	Erlin Arvelina
Address	Jl. Trsn. Gegerkalong Hilir Ds. Ciwaruga
City	Bandung
Region	Jawa Barat
Country	Indonesia
Phone	022 201 3789 ext. 168, 169, 239
Fax	022 201 3889
Administrator E-mail	erlin.arvelina@polban.ac.id
CKO E-mail	erlin.arvelina@polban.ac.id